Changzhou Junhe Technology Stock Co.,Ltd
| Supply Ability | 2 Tons per Day |
| Delivery Time | Ten days after receipt of advance payment |
| Packaging Details | Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A |
| Color | Silver |
| PH | 3.8-5.2 |
| Specific gravity | 1.30±0.05 |
| Viscosity | 20~60s(Spray Coating) 60~90S(Dip-Spin Coating) |
| Cr6+ | ≥25g/L |
| name | Zinc Coating |
| Brand Name | JUNHE |
| Model Number | 310B |
| Certification | ISO9001 TS16949 |
| Place of Origin | Changzhou in china |
View Detail Information
Explore similar products
Low Friction Dacromet Coating Friction Coefficient Of Small 0.12-0.18 PH 3.8-5.2
Self Dry Silver Top Coat Zinc Aluminium Flake Coating Acid Resistance PH 3.8-5.2
JUNHE Dacromet Coated Bolts Corrosion Protection Specific Gravity 1.30±0.05
Water Base Dacromet Coating With Good Leveling Adhesion PH Value Is 3.8-5.2
Product Specification
| Supply Ability | 2 Tons per Day | Delivery Time | Ten days after receipt of advance payment |
| Packaging Details | Pack A:16kg/ Metal Barrel Pack B:24KG Plastic Barrel Pack C:Based on the amount of B agent A | Color | Silver |
| PH | 3.8-5.2 | Specific gravity | 1.30±0.05 |
| Viscosity | 20~60s(Spray Coating) 60~90S(Dip-Spin Coating) | Cr6+ | ≥25g/L |
| name | Zinc Coating | Brand Name | JUNHE |
| Model Number | 310B | Certification | ISO9001 TS16949 |
| Place of Origin | Changzhou in china | ||
| High Light | Dip Spin Coating ，Zinc Aluminium Flake Coating | ||
Low Form Dip Spin Coating / High Dipping Speed Electroplated Zinc Coating
Dacromet anti-corrosion coating characteristics
1.1 anti-corrosion mechanism Dacromet coating, the appearance of matte silver gray, from the very fine sheet metal zinc, aluminum and chromate and other ingredients. After the workpiece in the degreasing, shot blasting treatment, dip Tu Duo Luo liquid.
Dacromet liquid is a water-based treatment solution, metal parts in the water-based treatment solution dip or spray, and then into the furnace curing, about 300 ℃ baking film, and the formation of zinc, aluminum, chromium inorganic coating Floor.
2. Coating Process
Mix Ratio
Pack A:16.0 kg
Pack B:24.0 kg (the quantity can be increased appropriately if spray coating)
Pack C:0-50 g (according to different viscosity demand )
3
Mixture Method |
Before Mixture, Keep weighted A&B into the water bath at 25±2℃ , then stir A to make metal slurry disperse uniformly by frequency mixer ,after A is fully evenly dispersed, reduce the agitating speed to 60r/min, and add B. 3.2.2 |
Add B to the stirring A slowly. At the moment ,the barrel temperature will go up,when it reaches 35℃, startup refrigerating device to keep the barrel temperature constant at 35℃. |
4. Technical data
| No. | Item | Data |
| 1 | PH | 3.8-5.2 |
| 2 | Cr6+ | ≥25g/L |
| 3 | Specific gravity | 1.30±0.05 |
| 4 | Viscosity | 20~60s(Spray Coating) ; 60~90S(Dip-Spin Coating) . 20℃ Zahn 2# cup |
| 5 | Operating temperature | 22±2℃ |
5. Coating Process
6.1 Degreasing
The workpiece should be degreased if there is oil on the surface. There are three processing methods:
1.High temperature
2.Neutral water-base degreasing agent
3.Organic solvent such as methylene chloride.
6.2 Derusting
The workpiece can not be coated if there is rust or burr on the surface.The best processing method is shot blasting. The corrosion resistance of coating will be effected if acid cleaning adopted.
6.3 Coating
The workpiece afer degreasing and shot blasting should be coated through Dip-Spin coating or Spraying Coating.
6.4 Pre-heating
The workpiece after coated should be Pre-heated as soon as possible at 80~150℃ for 8~15 mins to evaporate. ( according to heat absorption of workpiece.)
6.5 Curing
The workpiece after pre-heating should be cured at 300-340℃ for 20-40 mins. ( according to heat absorption of workpiece.)
Company Details
Business Type:
Manufacturer
Year Established:
1998
Total Annual:
1300-1500
Employee Number:
200~250
Ecer Certification：
Verified Supplier
Changzhou Junhe Technology Stock Co., Ltd. is a high-tech enterprise devoted to developing industrial fine chemicals, special equipment and services solution provider which was founded in Changzhou, Jiangsu in 1998. Zinc flake microlayer corrosion protection coating is one of our core p... Changzhou Junhe Technology Stock Co., Ltd. is a high-tech enterprise devoted to developing industrial fine chemicals, special equipment and services solution provider which was founded in Changzhou, Jiangsu in 1998. Zinc flake microlayer corrosion protection coating is one of our core p...