Shanghai Aboom Metal prodcut co.,ltd
| Payment Terms | T/T |
| Supply Ability | 200 tons per week |
| Delivery Time | 7-15dyas |
| Packaging Details | Standard export packaging |
| TYPE OF MATERIAL | Nickel-based corrosion resistant alloy |
| PRODUCT | ASTM B575 Hastelloy C-276 Hastelloy Alloy |
| STANDARD | ASTM B575 |
| GRADE | Hastelloy C-276 / N10276 / 2.4819 |
| Manufacturing process | The steel melt shall be refined with AOD or equivalent. |
| Type | plate / sheet / coil |
| Surface Finish | Pickled And Annealed, Bright Annealed, Polished |
| testing facility | Accept third-party testing such as SGS |
| Brand Name | ABOOM |
| Model Number | Hastelloy C-276 |
| Certification | EN 10204 Type 3.1 |
| Place of Origin | CHINA |
View Detail Information
Explore similar products
NS3201 Hastelloy B Seamless Pipe Nickel Molybdenum Alloy
N10001 HB Hastelloy Alloy Nickel Molybdenum Alloy Seamless Tube Hastelloy B
ASTM SB622 Hastelloy Material N10001 HB Hastelloy B Nickel Molybdenum Alloy
SB619 SB626 Hastelloy C-276 Pipe Flange Fittings For Drying Equipment
Product Specification
| Payment Terms | T/T | Supply Ability | 200 tons per week |
| Delivery Time | 7-15dyas | Packaging Details | Standard export packaging |
| TYPE OF MATERIAL | Nickel-based corrosion resistant alloy | PRODUCT | ASTM B575 Hastelloy C-276 Hastelloy Alloy |
| STANDARD | ASTM B575 | GRADE | Hastelloy C-276 / N10276 / 2.4819 |
| Manufacturing process | The steel melt shall be refined with AOD or equivalent. | Type | plate / sheet / coil |
| Surface Finish | Pickled And Annealed, Bright Annealed, Polished | testing facility | Accept third-party testing such as SGS |
| Brand Name | ABOOM | Model Number | Hastelloy C-276 |
| Certification | EN 10204 Type 3.1 | Place of Origin | CHINA |
| High Light | ASTM B575 hastelloy c276 sheet ，2.4819 hastelloy c276 sheet ，ASTM B575 hastelloy c276 plate | ||
ASTM B575 Hastelloy C-276 Hastelloy Alloy
Hastelloy C-276 / N10276 / 2.4819 Nickel Based plate
Some typical applications of HASTELLOY C276 include equipment components in chemical and petrochemical organic chloride processes and processes utilizing halide or acid catalysts. Other industry applications are pulp and paper (digesters and bleach areas), scrubbers and ducting for flue gas desulfurization, pharmaceutical and food processing equipment.
Regular size(mm) of ASTM B575 Hastelloy C-276 :
| Cold rolled sheet 1.0 * 1219 * C 1.5 * 1219 * C 2.5 * 1219 * C 3.0 * 1219 * C | Hot rolled sheet 4.0 * 1500 * c 5.0 * 1500 * c 8.0 * 1500 * c 10 * 1500 * c 14 * 1500 * c 16 * 1500 * 6000 18 * 1500 * 6000 20 * 1500 * 6000 30 * 1500 * 6000 |
Length:
As your requirement.
Applications of ASTM B575 Hastelloy C-276:
| Digesters and bleach plants in the paper industry. |
| Components exposed to sour gas. |
| Equipment for flue-gas desulfurisation plants. |
| Evaporators, heat exchangers, filters and mixers used in sulfuric acid environments. |
| Sulfuric acid reactors. |
| Organic chloride process equipment. |
| Equipment for processes utilizing halide or acid catalysts. |
Chemical Requirements | |||||||
|---|---|---|---|---|---|---|---|
|
| Ni | Cr | Mn | Mo | C | Si | Fe |
| Max % | Bal. | 16.5 | 1.0 | 17.0 | 0.010 | 0.08 | 7.0 |
| Min % | 14.5 | 15.0 | 4.0 | ||||
Mechanical Property Requirements | |||||
|---|---|---|---|---|---|
| Ultimate Tensile | Yield Strength (0.2% OS) | Elong. in 2 in. (50.8mm) or 4D min,% | R/A | Hardness | |
| Min | 100 KSi | 41 KSi | 40 | ||
| Max | |||||
| Min (Metric) | 690 MPa | 283 MPa | |||
| Max | |||||
Chart of Average Tensile Data At Temperatures
Specifications | |
|---|---|
| Form | Standard |
| UNS | UNS N10276 |
| Bar | ASTM B574 Din 17752 |
| Wire |
|
| Sheet | ASTM B575 Din 17750 |
| Plate | ASTM B575 Din 17750 |
| Fitting | ASTM B366 |
| Forging | ASTM B564 |
| Tube | ASTM B619 ASTM B622 ASTM B626 Din 17751 |
| Pipe | ASTM B619 ASTM B622 ASTM B626 Din 17751 |
| Weld Wire | A5.14 ERNiCrMo-4 |
| Weld Electrode | A5.11 ENiCrMo-4 |
| Din. | 2.4819 All Forms |
| Table 16 | |
|---|---|
| RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS | |
| Operations | Carbide Tools |
| Roughing, with severe interruption | Turning or Facing C-2 and C-3 grade: Negative rake square insert, 45 degree SCEA1, 1/32 in. nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 30-50 sfm, 0.004-0.008 in. feed, 0.150 in depth of cut. Dry2, oil3, or water-base coolant4. |
| Normal roughing | Turning or Facing C-2 or C-3 grade: Negative rate square insert, 45 degree SCEA, 1/32 in nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 90 sfm depending on rigidity of set up, 0.010 in. feed, 0.150 in. depth of cut. Dry, oil, or water-base coolant. |
| Finishing | Turning or Facing C-2 or C-3 grade: Positive rake square insert, if possible, 45 degree SCEA, 1/32 in. nose radius. Tool holder: 5 degree pos. back rake, 5 degree pos. side rake. Speed: 95-110 sfm, 0.005-0.007 in. feed, 0.040 in. depth of cut. Dry or water-base coolant. |
| Rough Boring | C-2 or C-3 grade: If insert type boring bar, use standard positive rake tools with largest possible SCEA and 1/16 in. nose radius. If brazed tool bar, grind 0 degree back rake, 10 degree pos. side rake, 1/32 in. nose radius and largest possible SCEA. Speed: 70 sfm depending on the rigidity of setup, 0.005-0.008 in. feed, 1/8 in. depth of cut. Dry, oil or water-base coolant. |
| Finish Boring | C-2 or C-3 grade: Use standard positive rake tools on insert type bars. Grind brazed tools as for finish turning and facing except back rake may be best at 0 degrees. Speed: 95-110 sfm, 0.002-0.004 in feed. Water-base coolant. |
| Notes: | |
| 1 SCEA - Side cutting edge angle or lead angle of the tool. 2 At any point where dry cutting is recommended, an air jet directed on the tool may provide substantial tool life increases. A water-base coolant mist may also be effective. 3 Oil coolant should be premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degrees F from 50 to 125 SSU. 4 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix. Water-base coolant may cause chipping and rapid failure of carbide tools in interrupted cuts. | |
| Table 17 | |
|---|---|
| RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS | |
| Operations | Carbide Tools |
| Facing Milling | Carbide not generally successful, C- grade may work. Use positive axial and radial rake, 45 degree corner angle, 10 degree relief angle. Speed: 50-60 sfm. Feed: 0.005-0.008 in. Oil or waterbase coolants will reduce thermal shock damage of carbide cutter teeth. |
| End Milling | Not recommended , but C-2 grades may be successful on good setups. Use positive rake. Speed: 50-60 sfm. Feed: Same as high speed steel. Oil or water-base coolants will reduce thermal shock damage. |
| Drilling | C-2 grade not recommended, but tipped drills may be successful on rigid setup if no great depth. The web must thinned to reduce thrust. Use 135 degree included angle on point. Gun drill can be used. Speed: 50 sfm. Oil or water-base coolant. Coolant-feed carbide tipped drills may be economical in some setups. |
| Reaming | C-2 or C-3 grade: Tipped reamers recommended, solid carbide reamers require vary good setup. Tool geometry same as high speed steel. Speed: 50 sfm. Feed: Same as high speed steel. |
| Tapping | Not recommended, machine threads, or roll-form them. |
| Electrical Discharge Machining | The alloys can be easily cut using any conventional electrical discharge machining system (EDM) or wire (EDM). |
| Notes: | |
| 5 M-40 series High Speed Steels include M-41 , M-42, M-43, M-44, M-45 and M-46 at the time of writing. Others may be added and should be equally suitable. 6 Oil coolant should be a premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degree F from 50 to 125 SSU. 7 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix. | |
| Table 18 | |
|---|---|
| Plasma Arc Cutting | |
| Our alloys can be cut using any conventional plasma arc cutting system. The best arc quality is achieved using a mixture of argon and hydrogen gases. Nitrogen gas can be substituted for hydrogen gases, but the cut quality will deteriorate slightly. Shop air or any oxygen bearing gases should be avoided when plasma cutting these alloys. | |
SHANGHAI ABOOM METAL PRODUCT CO.,LTD
Address:ROOM 412,NO.452 CHEFENG ROAD,
SongjiangDistrict , Shanghai ,201601,P.R.China
Company Details
Business Type:
Manufacturer
Employee Number:
>100
Ecer Certification：
Active Member
Shanghai Aboom Metal prodcut co.,ltd mainly produces and sells super duplex stainless steel, special super austenitic stainless steel and high temperature alloys, nickel-based alloys, corrosion-resistant alloys, precisio... Shanghai Aboom Metal prodcut co.,ltd mainly produces and sells super duplex stainless steel, special super austenitic stainless steel and high temperature alloys, nickel-based alloys, corrosion-resistant alloys, precisio...