JIANGSU MITTEL STEEL INDUSTRIAL LIMITED
| Payment Terms | L/C, Western Union, T/T |
| Supply Ability | 500Tons |
| Delivery Time | 7 Days |
| Packaging Details | Wooden Pallet |
| Material | Metal,stainless steel 304H S30409 |
| Size | Customized Size 4*8 FEET 5*10 FEET |
| Shape | flat Plate |
| Thickness | 1-30mm |
| Packing | Wooden Pallet |
| Surface | According to customer demand |
| Brand Name | TSING SHAN |
| Model Number | 304H S30409 |
| Certification | ISO MTC SGS |
| Place of Origin | China |
View Detail Information
Explore similar products
409L Stainless Steel Plate Stainless 409 ,Grade UNS40900 SUH409L Sheet 2D
SUH409L Stainless Steel Plate 1D Finished 3-10mm Hot Rolled Stainless Steel 409L
ASTM A240 SS316L TP316L Stainless Steel Plates 2000*6000mm Floor / Corrosion
ASTM A240 / A240M AISI 316LN DIN 1.4429 Stainless Steel Sheets And Plates 2B And
Product Specification
| Payment Terms | L/C, Western Union, T/T | Supply Ability | 500Tons |
| Delivery Time | 7 Days | Packaging Details | Wooden Pallet |
| Material | Metal,stainless steel 304H S30409 | Size | Customized Size 4*8 FEET 5*10 FEET |
| Shape | flat Plate | Thickness | 1-30mm |
| Packing | Wooden Pallet | Surface | According to customer demand |
| Brand Name | TSING SHAN | Model Number | 304H S30409 |
| Certification | ISO MTC SGS | Place of Origin | China |
| High Light | 304H stainless flat plate ，11 Gauge stainless flat sheet ，4x8 Feet flat plate stainless steel | ||
Alloy 304/304H (UNS S30400/ S30409) is a modification of the most widely utilized "18-8" chromium-nickel austenitic stainless steel. The carbon content is controlled in the range of 0.04-0.10% for increased strength at temperatures above 800°F (427°C). It is an economical and versatile corrosion resistant alloy suitable for a wide range of general purpose applications.
It is common practice for 304H to be dual certified as 304 and 304H. The high carbon chemistry of 304H enables 304 to meet the mechanical properties and grain size requirements of 304H.
Alloy 304/304H has general corrosion resistance similar to 304/304L. It resists atmospheric corrosion, as well as, moderately oxidizing and reducing environments. However, because of its high carbon content, Alloy 304/304H is subject to carbide precipitation in the heat affected zone of welds.
Alloy 304/304H is non-magnetic in the annealed condition, but can become slightly magnetic as a result of cold working or welding. It can be easily welded and processed by standard shop fabrication practices.
Alloy 304/304H has good resistance to atmospheric corrosion, foods and beverages and to many organic and inorganic chemicals in moderately oxidizing to moderately reducing environments. The high chromium content of the alloy provides resistance to oxidizing solutions such as nitric acid up to 55% weight and up to 176°F (80°C).
Alloy 304/304H also resists moderately aggressive organic acids such as acetic. The nickel present in the alloy provides resistance to moderately reducing solutions such as pure phosphoric acid, whatever the concentration, in cold solutions and up to 10% diluted hot solutions. The alloy can also operate successfully in caustic solutions free of chlorides or fluorides at moderate temperatures.
Alloy 304/304H does not perform well in more highly reducing environments such as those containing chlorides and sulfuric acid.
Alloy 304/304H performs well in fresh water service with low levels of chlorides (less than 100ppm). At higher chloride levels the grade is susceptible to crevice corrosion and pitting. For successful performance under these more severe conditions, higher molybdenum content is need such as 316/316L. Alloy 304/304H is not recommended for service in marine environments.
In most instances, the corrosion resistance of Alloys 304, 304L and 30H will be roughly equal in most corrosive environments. However, in environments that are sufficiently corrosive to cause intergranular corrosion of welds and heat-affected zones Alloy 304L should be used because of its low carbon content.
Lowest Temperature (°F) at Which the Corrosion Rate Exceeds 5mpy
| CORROSION ENVIRONMENT | Type 304/304H | Type 316L | 2205 (UNS S32205) | 2507 |
|---|---|---|---|---|
| 0.2% Hydrochloric Acid | >Boiling | >Boiling | >Boiling | >Boiling |
| 1% Hydrochloric Acid | 86p | 86 | 185 | >Boiling |
| 10% Sulfuric Acid | — | 122 | 140 | 167 |
| 60% Sulfuric Acid | — | <54 | <59 | <57 |
| 96% Sulfuric Acid | — | 113 | 77 | 86 |
| 85% Phosphoric Acid | 176 | 203 | 194 | 203 |
| 10% Nitric Acid | >Boiling | >Boiling | >Boiling | >Boiling |
| 65% Niitric Acid | 212 | 212 | 221 | 230 |
| 80% Acetic Acid | 212p | >Boiling | >Boiling | >Boiling |
| 50% Formic Acid | ≤50 | 104 | 194 | 194 |
| 50% Sodium Hydroxide | 185 | 194 | 194 | 230 |
| 83% Phosphoric Acid + 2% Hydrofluoric Acid | 113 | 149 | 122 | 140 |
| 60% Nitric Acid + 2% Hydrocloric Acid | >140 | >140 | >140 | >140 |
| 50% Acetic Acid + 50% Acetic Anhydride | >Boiling | 248 | 212 | 230 |
| 1% Hydrochloric Acid + 0.3% Ferric Chloride | 68p | 77p | 113ps | 203ps |
| 10% Sulfuric Acid + 2000ppm Cl- + N2 | — | 77 | 95 | 122 |
| 10% Sulfuric Acid + 2000ppm Cl- + SO2 | — | <<59p | <59 | 104 |
| WPA1, High Cl- Content | <<50 | ≤50 | 113 | 203 |
| WPA2, High F- Content | <<50 | ≤50 | 140 | 167 |
ps = pitting can occur
ps = pitting/crevice corrosion can occur
| WPA | P2O5 | CL- | F- | H2SO4 | Fe2O3 | Al2O3 | SiO2 | CaO | MgO |
|---|---|---|---|---|---|---|---|---|---|
| 1 | 54 | 0.20 | 0.50 | 4.0 | 0.30 | 0.20 | 0.10 | 0.20 | 0.70 |
| 2 | 54 | 0.02 | 2.0 | 4.0 | 0.30 | 0.20 | 0.10 | 0.20 | 0.70 |
Weight % (all values are maximum unless a range is otherwise indicated)
| Element | 304 | 304H |
|---|---|---|
| Chromium | 18.0 min.-20.0 max. | 18.0 min.-20.0 max. |
| Nickel | 8.0 min.-10.5 max. | 8.0 min.-10.5 max. |
| Carbon | 0.08 | 0.04 min-0.10 max. |
| Manganese | 2.00 | 2.00 |
| Phosphorus | 0.045 | 0.045 |
| Sulfer | 0.030 | 0.030 |
| Silicon | 0.75 | 0.75 |
| Nitrogen | 0.10 | 0.10 |
| Iron | Balance | Balance |
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Agent,Exporter,Seller
Year Established:
1998
Total Annual:
80Millen-100 Millen
Employee Number:
200~500
Ecer Certification：
Verified Supplier
Jiangsu Mittel Steel Industrial Limited is located in Wuxi City, a beautiful city near Shanghai. Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transporta... Jiangsu Mittel Steel Industrial Limited is located in Wuxi City, a beautiful city near Shanghai. Wuxi is close to Shanghai (BAO STEEL) ,Zhangjiagang (ZPSS),Ningbo (BAO XIN),KUN SHAN (DKSS), enjoy excellent geographic location and convenient water, land and air transporta...