Product Specification

High Hardness 420 Stainless Steel Strip 0.6 - 8.0mm for Knife SS Strip Width 6 - 500mm

STAINLESS STEEL 420 STRIP GENERAL PROPERTIES:

Stainless Steel 420 is a hardenable, martensitic stainless steel that is a modification of Alloy 410. Similar to 410, it contains a minimum of 12% chromium, just sufficient enough to give corrosion resistant properties. Alloy 420 has higher carbon content than Alloy 410 which is designed to optimize strength and hardness characteristics. It has good ductility it the annealed condition but is capable of being hardened up to Rockwell hardness 50 HRC, the highest hardness of the 12% chromium grades. Due to its hardening properties, Stainless Steel 420 is not often welded, although it is possible. Martensitic stainless steels are designed for high hardness and sometimes other properties are to some degree compromised. Corrosion resistance is lower than the common austenitic grades and their useful operating range is limited by their loss of ductility at sub-zero temperatures and loss of strength by over-tempering at elevated temperatures. Its best corrosion resistance is achieved when the metal is hardened and surface ground or polished.

We Export and Supply Stainless steel 420 strips capabilities include:

• Stainless steel 420 strips Annealed & Precision
• Stainless steel 420 strips thickness-0.1mm to 6.00mm
• Stainless steel 420 strips width-2.5mm to 1320mm (slit to close tolerances)

We provides Stainless steel 420 Cold rolled mill finish strips such as:

• Stainless steel 420 strips 2D - cold rolled, heat treated, pickled.
• Stainless steel 420 strips 2B - cold rolled, heat treated, pickled, skin passed on bright rolls.
• Stainless steel 420 strips 2R(BA) - cold rolled, bright annealed
• Stainless steel 420 strips HR - hot rolled, annealed

STAINLESS STEEL 420 STRIP APPLICATIONS:

Stainless Steel 420 is used for a variety of applications where good corrosion and outstanding hardness is necessary. It is not usually used at temperatures exceeding 800°F (427°C) due to quick hardening and loss of corrosion resistance. Examples of applications that use alloy 420 include:

• Cuttery
• Knife blades
• Surgical instruments
• Needle valves
• Shear blades
• Scissors
• Hand tools

STAINLESS STEEL 420 STRIP CORROSION RESISTANCE:

• Less resistant than the austenitic grades and the 17% chromium ferritic alloys
• Good resistance in the hardened condition to the atmosphere, foods, fresh water, and mild acids
• Resistance lowered in the annealed condition
• Best with a smooth surface finish

STAINLESS STEEL 420 STRIP HEAT RESISTANCE:

• Not recommended for use above the relevant tempering temperature because of reduction in mechanical properties
• Scaling temperature is approximately 1202°F (650°C)

STAINLESS STEEL 420 STRIP WELDING:

• Not commonly welded due to air hardening characteristics.
• Welding may be performed after preheating to 300-400 F
• Post weld tempering at temperature for 2 hours

STAINLESS STEEL 420 STRIP HOT WORKING:

• Recommended to bring temperatures slowly up to 1400, then on to 2000-2200 F
• Furnace cool slowly to avoid cracking, after furnace working
• Reheating is necessary to keep working temperature above 1600 F.

STAINLESS STEEL 420 STRIP COLD WORKING:

• Can withstand only minor cold work.
• Radical forming operations will result in cracking.

STAINLESS STEEL 420 STRIP ANEALING:

• Anneal at temperatures between 1550-1650 F (843-900 C)
• Allow for slow furnace cooling.

STAINLESS STEEL 420 STRIP TEMPERING:

• Temper at temperatures of 300-400 F
• Air cool for maximum hardness and corrosion resistance.

STAINLESS STEEL 420 STRIP HARDENING:

• Soak at 1850-1950 F to quench in heated oil.