Qingdao Teste Metal Products Co., Ltd.
| Payment Terms | L/C, T/T, Western Union |
| Supply Ability | 5000 Ton/Tons per Month |
| Delivery Time | 7~10 working days |
| Product name | Alloy Steel Round Bar |
| Heat-treatment | +A,+N,+NT,+QT |
| Diameter | 3mm~3000mm |
| Surface | Black,Grounded,Peeled/Turned,Polished |
| Certification | ISO 9001 ,CE |
| Place of Origin | Jiangsu,China |
View Detail Information
Explore similar products
SCM440 Alloy Steel Products Alloy Steel Rod Forged 42crmo4 Round Bar
Flat Rolled Alloy Steel Products AISI 4140 Steel Rectangular Bar 42CrMo4 SCM440
25CrMo4 20mncr5 Round Bar For Construction Mild Steel AISI 4130 SCM430 1.7147
5160 5052 6150 4150 4130 4140 Alloy Steel Round Bar 42crmo4 AISI 5140 41Cr4
Product Specification
| Payment Terms | L/C, T/T, Western Union | Supply Ability | 5000 Ton/Tons per Month |
| Delivery Time | 7~10 working days | Product name | Alloy Steel Round Bar |
| Heat-treatment | +A,+N,+NT,+QT | Diameter | 3mm~3000mm |
| Surface | Black,Grounded,Peeled/Turned,Polished | Certification | ISO 9001 ,CE |
| Place of Origin | Jiangsu,China | ||
| High Light | en 353 alloy steel round bar ，4340 alloy steel round bars ，en24 alloy steel | ||
AISI 4340 steel is a medium carbon, low alloy steel known for its toughness and strength in relatively large sections. AISI 4340 is also one kind of nickel chromium molybdenum steels. 4340 alloy steel is generally supplied hardened and tempered in the tensile range of 930 – 1080 Mpa. Pre hardened and tempered 4340 steels can be further surface hardened by flame or induction hardening and by nitriding. The 4340 steel has good shock and impact resistance as well as wear and abrasion resistance in the hardened condition. AISI 4340 steel properties offer good ductility in the annealed condition, allowing it to be bent or formed. Fusion and resistance welding is also possible with our 4340 alloy steel. ASTM 4340 material is often utilized where other alloy steels do not have the hardenability to give the strength required. For highly stressed parts it is excellent choice.
CHEMICAL COMPOSITION
| Element | C | Mn | Si | P | S | Mo |
| 4140 | 0.38~0.43% | 0.75~1.0% | 0.15~0.30% | 0.035% | 0.04% | 0.15~0.25% |
| 4130 | 0.28~0.33% | 0.70~0.90% | 0.15~0.35% | 0.035% | 0.04% | 0.15~0.25% |
| 4340 | 0.38%~0.43% | 0.60~0.80% | 0.15~0.35% | 0.035% | 0.04% | 0.20~0.30% |
| 5140 | 0.38~0.48% | 0.70~0.9% | 0.15~0.35% | 0.035% | 0.04% | - |
HEAT TREATMENT OPTION
FABRICATION AND HEAT TREATMENT
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.
Stress Relieving
For pre-hardened steel stress relieving is achieved by heating steel 4340 to between 500 to 550°C. Heat to 600 °C – 650 °C, hold until temperature is uniform throughout the section, soak for 1 hour per 25 mm section, and cool in still air.
Annealing
A full anneal may be done at 844°C (1550 F) followed by controlled (furnace) cooling at a rate not faster than 10°C (50 F) per hour down to 315°C (600 F). From 315°C 600 F it may be air cooled.
Tempering
AISI 4340 alloy steel should be in the heat treated or normalized and heat treated condition before tempering. The tempering temperature for depends upon the strength level desired. For strength levels in the 260 – 280 ksi range temper at 232°C (450 F). For strength in the 125 – 200 ksi range temper at 510°C (950 F). And don’t temper the 4340 steels if it is in the 220 – 260 ksi strength range as tempering can result in degradation of impact resistance for this level of strength.
Tempering should be avoided if possible within the range 250 °C – 450 °C due to temper brittleness.
Company Details
Business Type:
Manufacturer,Exporter,Trading Company,Seller
Year Established:
2018
Total Annual:
15000000-20000000
Employee Number:
100~120
Ecer Certification：
Verified Supplier
Qingdao Teste Metal Products Co., Ltd. is a professional manufacturer with more than 20 years of experience in manufacturing stainless steel and carbon steel establised in 2018. Our location is in Wuxi - the largest stainless-steel processing center in China. We have our own factory and... Qingdao Teste Metal Products Co., Ltd. is a professional manufacturer with more than 20 years of experience in manufacturing stainless steel and carbon steel establised in 2018. Our location is in Wuxi - the largest stainless-steel processing center in China. We have our own factory and...
Get in touch with us
Leave a Message, we will call you back quickly!