| Name | H13 Die Steel Bar |
| Material | H13 |
| Diameter | 6.0mm-500mm |
| Length | 2.5m-10m |
| Type | ASTM A681-2008 |
| Application | Suitable for tool steel with complex deformation, various kinds of cold stamping dies with high wear resistance and long service life, cold cutting blades, and thread rolling plates; Cold extrusion forming, drawing film, stainless steel sheet and balance c |
| Brand Name | Zhanlu |
| Model Number | H13 |
| Place of Origin | China |
View Detail Information
Explore similar products
Aisi D3 Tool Steel Bar Suppliers Din 1.2080 X210cr12 Steel DIN EN X210Cr12 BS
D2 1.2379 S45c Skd11 Tool Steel Bar Cutting JIS G4404 2006 Cr12MoV
Plat Suj2 Skd11 AISI SAE D3 Die Steel Bar DIN EN X210Cr12 BS X210Cr12 Cr12mov
Jis SKD11 Aisi Die Steel Bar JIS G4404-2006 Cr12mov Steel Equivalent
Product Specification
| Payment Terms | L/C, T/T | Supply Ability | Consulting service |
| Delivery Time | 5-8Workdays | Packaging Details | Conventional packaging |
| Name | H13 Die Steel Bar | Material | H13 |
| Diameter | 6.0mm-500mm | Length | 2.5m-10m |
| Type | ASTM A681-2008 | Application | Suitable for tool steel with complex deformation, various kinds of cold stamping dies with high wear resistance and long service life, cold cutting blades, and thread rolling plates; Cold extrusion forming, drawing film, stainless steel sheet and balance c |
| Brand Name | Zhanlu | Model Number | H13 |
| Place of Origin | China | ||
| High Light | h13 tool steel heat treatment ，aisi h13 steel ，astm a681 h13 | ||
H13 is widely used for aluminum and zinc casting dies, as well as for aluminum extrusion, aluminum die casting and press tooling. This grade is ideal for a range of hot work and cold work applications—particularly hot work applications where drastic cooling is required throughout its operation.
For hot work applications, H13 is used in the hardness range of HRC 38 to 48. The usual hardness range for die casting dies is HRC 44 to 48 requiring a temper at approximately 1100°F. For improved shock resistance, the steel is often tempered at temperatures approaching 1150°F, resulting in hardnesses of HRC 40 to 44.
Supply Form & Size
| Form of Supply | Size(mm) | Length(mm) |
| Round bar | 6.0mm-500mm | 2.5m-10m |
Chemical Composition&Related Specifications
| Grade | C | Mn | Cr | Mo | V | P | S | Si |
| H13 | 0.32~0.45 | 0.2-0.50 | 4.75~5.50 | 1.10~1.75 | 0.8~1.2 | ≤0.030 | ≤0.030 | 0.8~1.2 |
Brand comparison table
| AISI/SAE | DIN/EN | BS | JIS/KS | China |
| H13 | X40CrMoV5-1 | X40CrMoV5-1 | SKD61 | 4Cr5MoSiV1 |
4) Mechanical Properties - Mechanical Property
1. Pre-heat treatment The H13 steel steel and die blank supplied on the market have been annealed heat treatment in the steel mill to ensure good metallographic structure, appropriate hardness, good processability, and no need for annealing. However, after the manufacturer carried out the forging, the original structure and properties were destroyed, which increased the forging stress, and had to be reannealed.
The isothermal spheroidization annealing process is: 860~890 °C heating and insulation for 2h, cooling to 740~760 °C isothermal 4h, furnace cooling to about 500 °C out of the oven.
2. Quenching and tempering Mold quenching process specifications requiring good toughness: heating temperature 1020~1050 °C, oil cooling or air cooling, hardness 54~58HRC; It requires hot hardness based mold quenching process specifications, heating temperature 1050~1080 °C, oil cooling, hardness 56~58HRC.
Recommended tempering temperature: 530~560°C, hardness 48~52HRC; Tempering temperature 560~580°C; Hardness 47~49HRC.
Tempering should be performed twice. When tempering at 500 °C, the tempering secondary hardening peak occurs, and the tempering hardness is the highest, the peak is about 55HRC, but the toughness is the worst. Therefore, the tempering process should avoid about 500 °C. According to the use of mold, tempering is better in the range of 540~620 °C.
Quenching heating should be preheated twice (600~650 °C, 800~850 °C) to reduce the thermal stress generated by the heating process.
3. Chemical heat treatment H13 steel can further strengthen the mold if it is gas nitriding or nitrocarburizing, but its nitriding temperature should not be higher than the tempering temperature to ensure that the core strength is not reduced, thereby improving the service life of the mold.
Company Details
Business Type:
Distributor/Wholesaler
Year Established:
2016
Total Annual:
5000000-10000000
Employee Number:
5~20
Ecer Certification：
Verified Supplier
Wuxi Zhanlu International Trade Co., Ltd.: Our company's address is located in Wuxi, Jiangsu Province, China, where the steel resources are very rich. Our company is a comprehensive import and export steel trade enterprise. We can provide steel trade, logistics, warehousing and other services. O... Wuxi Zhanlu International Trade Co., Ltd.: Our company's address is located in Wuxi, Jiangsu Province, China, where the steel resources are very rich. Our company is a comprehensive import and export steel trade enterprise. We can provide steel trade, logistics, warehousing and other services. O...