Xiamen WangQin Chemical Technology Co., Ltd.
| Supply Ability | 500t/month |
| Delivery Time | 14 work days |
| Packaging Details | 25kg/bag |
| Appearance | Brown viscous liquid |
| Non-Volatile Matter ( %) | 74±2.0 |
| Viscosity (25℃， mPa.s) | ≤200 |
| name | Water Based Industrial Coating Resins |
| color | white or transparent |
| pH | 8.0-9.0 |
| Brand Name | WeiLi Resin® |
| Model Number | WL-172B |
| Certification | ISO9001 |
| Place of Origin | China |
View Detail Information
Explore similar products
Water Based Hydroxyl Acrylic Resin Impact Resistance And Solvent Resistance
WL -174 Water Soluble Epoxy Ester Resin Excellent Water And Corrosion Resistance
Cross - Linking Monomer Aqueous Acrylic Resin Environmentally Safe And Low In VO
Low VOC Low Odor Water Based Epoxy Curing Agents Fast Dry Properties
Product Specification
| Supply Ability | 500t/month | Delivery Time | 14 work days |
| Packaging Details | 25kg/bag | Appearance | Brown viscous liquid |
| Non-Volatile Matter ( %) | 74±2.0 | Viscosity (25℃， mPa.s) | ≤200 |
| name | Water Based Industrial Coating Resins | color | white or transparent |
| pH | 8.0-9.0 | Brand Name | WeiLi Resin® |
| Model Number | WL-172B | Certification | ISO9001 |
| Place of Origin | China | ||
| High Light | waterborne epoxy resins ，water based resin ，Iron Oxide Primer Epoxy Ester Resin | ||
Waterborne Epoxy Ester Resin WL-172B
A red iron oxide primer and topcoat made of the water soluble epoxy ester resin WL-172B have high-performance, single-component, quick-dry, rust preventive formulated for use on ferrous metal substrates. It provides corrosion resistance for both interior and exterior steel surfaces. It is formulated to provide lasting rust and corrosion resistance on a variety of interior and exterior metal surfaces and may be top coated with water-based or alkyd/oil-based finishes. This primer offers excellent coverage, spreads evenly, resists sagging, is abrasion resistant, and provides unsurpassed durability.
Product Properties:
Resin Composition:
Waterborne resin, cosolvent, neutralizer
Typical Data:
| Item | WL-172B | Test Method |
| Appearance | Brown viscous liquid | Visual Observation |
| Non-Volatile Matter ( %) | 74±2.0 | GB/T1725-2007 ( 30min@120℃) |
| Viscosity (25℃, mPa.s) | ≤200 | GB/T 21059-2007 NDJ-79 Rotational Viscometer Dilute with PM by 1:1 ratio, then test |
Recommending WL-172B high performance waterborne epoxy ester resin
WL-172B Iron Oxide Red Primer
Reference Formula:
| 1 | WL-172B |
| 2 | N,N-DMEA |
| 3 | Deionized Water |
| 4 | Dispersing Agent |
| 5 | Defoamer |
| 6 | Attapulgite |
| 7 | Iron Oxide Red |
| 8 | Zinc Sulphate |
| 9 | Precipitated Barium Sulphate |
| 10 | Deionized Water |
| 11 | WL-172B |
| 12 | N,N-DMEA |
| 13 | Drier |
| 14 | Sodium Nitrite |
| 15 | Deionized Water |
| 16 | Substrate Wetting Agent |
| 17 | Thickener |
Performance Data:
| No. | Test Item | Test Data | Test Standard |
| 1 | Original Paint Appearance | No lumps, stir evenly | Visual Observation |
| 2 | Paint Film Color | Iron red color | Visual Observation |
| 3 | Original Paint Viscosity(25℃)Ku | 80-90 | GB/T9269-2009 |
| 4 | pH | 8-9 | GB8325-1987 |
| 5 | Fineness μm | ＜35 | GB/T6753.1-2007 |
| 6 | Non-Volatile Matter Content % | 48 | GB/T1725-2007 |
| 7 | Surface Drying Time | ≤20min | GB1728-79 |
| 8 | Hard Drying Time | ≤5hrs | GB1728-79 |
| 9 | Gloss | 10 | GB/T9754-2007 |
| 10 | Hardness (Pencil Method) | HB | GB/T6739-1996 |
| 11 | Flexibility | 1mm | GB/T6742-2007 |
| 12 | Impact Resistance kg.cm | 50 | GB/T1732-1993 |
| 13 | Double Pendulum Hardness | 0.58 | GB/T1730-2007 |
| 14 | Adhesion (Cross-Cut Method) | 1grade | GB/T9286-1998 |
| 15 | Storage Stability | 50℃*4 weeks,no layering, no sedimentation | ———— |
Iron Oxide Red Primer Initial Water Resistance
Substrate:tinplate
Film thickness:23±3μm
| Time | Water Drenching Test Data |
| Air Drying 24hrs | 48hrs no abnormalities |
| Air Drying 72hrs | 96hrs no abnormalities |
| Air Drying 168hrs | 168hrs no abnormalities |
Iron Oxide Red Primer Anti- Corrosive Properties
Substrate:carbon steel plate
Film thickness:45±5μm
| Item | Test Data |
| Salt fog resistance | 72hrs no abnormalities |
| Salt water resistance | 120hrs no abnormalities |
WL-172B Iron Oxide Red Primer
Reference Formula:
| 1 | WL-172B |
| 2 | N,N-DMEA |
| 3 | Deionized Water |
| 4 | Dispersing Agent |
| 5 | Defoamer |
| 6 | Attapulgite |
| 7 | Titanium Dioxide |
| 8 | Carbon Black |
| 9 | Precipitated Barium Sulphate |
| 10 | Deionized Water |
| 11 | WL-172B |
| 12 | N,N-DMEA |
| 13 | Drier |
| 14 | Deionized Water |
| 15 | Substrate Wetting Agent |
| 16 | Thickener |
Performance Data:
| No. | Test Item | Test Data | Test Standard |
| 1 | Original Paint Appearance | No lump, stir evenly | Visual Observation |
| 2 | Paint Film Color | Gray | Visual Observation |
| 3 | Original Paint Viscosity(25℃)Ku | 80-90 | GB/T9269-2009 |
| 4 | pH | 8-9 | GB8325-1987 |
| 5 | Fineness μm | ＜30 | GB/T6753.1-2007 |
| 6 | Non-Volatile Matter Content % | 48 | GB/T1725-2007 |
| 7 | Surface Drying Time | ≤3min | GB1728-79 |
| 8 | Hard Drying Time | ≤16hrs | GB1728-79 |
| 9 | Gloss | 90-92 | GB/T9754-2007 |
| 10 | Hardness(pencil method) | HB | GB/T6739-1996 |
| 11 | Flexibility | 1mm | GB/T6742-2007 |
| 12 | Impact Resistance kg.cm | 50 | GB/T1732-1993 |
| 13 | Double Pendulum Hardness | 0.4 | GB/T1730-2007 |
| 14 | Adhesion(Cross-Cut Method) | 1grade | GB/T9286-1998 |
High Gloss Gray Topcoat Hardness Increase
Substrate:glass pane
Film thickness:23±3μm
Ambient temperature:25±5℃
Ambient humidity:50±2%
| Double Pendulum Hardness(glass pane) | ||
| Time | Drier 0.52% | Drier 0.85% |
| 24hrs | 0.19 | 0.22 |
| 48hrs | 0.25 | 0.27 |
| 72hrs | 0.28 | 0.32 |
| 120hrs | 0.53 | 0.53 |
High Gloss Gray Topcoat Initial Water Resistance
Substrate:tinplate
Film thickness:23±3μm
| Time | Water drenching before adjustment | Water drenching after adjustment |
| Air Drying 24hrs | 24hrs no abnormalities | 48hrs no abnormalities |
| Air Drying 72hrs | 44hrs no abnormalities | 56hrs no abnormalities |
| Air Drying 168hrs | 96hrs no abnormalities | 144hrs no abnormalities |
Company Details
Business Type:
Manufacturer,Importer,Exporter,Trading Company
Year Established:
2010
Employee Number:
10~50
Ecer Certification：
Verified Supplier
Established in 2010, Xiamen WangQin Chemical Technology is a professional corporation specializing in researching, developing manufacturer for different resin products. With a staff of 50 people, WangQin has been equipped with advanced manufacturing facilities and a full range of product testing equ... Established in 2010, Xiamen WangQin Chemical Technology is a professional corporation specializing in researching, developing manufacturer for different resin products. With a staff of 50 people, WangQin has been equipped with advanced manufacturing facilities and a full range of product testing equ...
Get in touch with us
Leave a Message, we will call you back quickly!