Xiamen WangQin Chemical Technology Co., Ltd.
| Payment Terms | L/C, T/T |
| Supply Ability | 500t/month |
| Delivery Time | 14 work days |
| Packaging Details | 200kg/drum |
| Appearance | Clear |
| Fe-Co Color | ≤1 |
| Viscosity Pa.s/25℃ | 1.0-1.8 |
| Non-volatile % | 70±2 |
| Acid value mgKOH/g | 6-10 |
| Hydroxyl value | 110 |
| Model Number | SE6783 |
| Certification | ISO9001 |
| Place of Origin | china |
| Brand Name | WeiLi Resin® |
View Detail Information
Explore similar products
High Fullness Solvent Based Acrylic Resin For Motorcycle Finishing Coat
Excellent Adhesion Solvent Based Acrylic Resin For Metallic Substrates
High Gloss Hydroxyl Acrylic Resin Metallic Top Coatings Excellent Durability
PU Coatings Solvent Based Acrylic Resin , Eco Friendly Resin For Spectacle
Product Specification
| Payment Terms | L/C, T/T | Supply Ability | 500t/month |
| Delivery Time | 14 work days | Packaging Details | 200kg/drum |
| Appearance | Clear | Fe-Co Color | ≤1 |
| Viscosity Pa.s/25℃ | 1.0-1.8 | Non-volatile % | 70±2 |
| Acid value mgKOH/g | 6-10 | Hydroxyl value | 110 |
| Model Number | SE6783 | Certification | ISO9001 |
| Place of Origin | china | Brand Name | WeiLi Resin® |
| High Light | clear acrylic resin ，eco friendly resin ，Low Viscosity Hydroxyl Acrylic Resin | ||
SE6783 is a two-component hydroxyl acrylic resin, it has high solid content, low viscosity, good weather resistance and other characteristics, due to the use of low molecular weight resin, the coating viscosity is greatly reduced, and because of the high solid content, thus reducing the content of organic compounds in the coating. It is a new kind of resin which has both performance and environmental protection. Therefore SE6783 is an environmentally friendly solvent based hydroxyl acrylic resin.
Recommended applications: automobile refinishing paint, motorcycle finishing varnish , topcoats for steel and plastics, solid color paints.
1. Features
High solid and low viscosity, high gloss, high fullness, excellent levelling property, excellent weather resistance, excellent chemical resistance and pigment dispersity.
2. Applications
PU top coat, motorcycle, home appliances cover light varnish, colored paint, automotive refinishing paint.
3. Properties
| Component | Appearance |
Fe-Co Color |
Viscosity Pa.s/25℃ |
Non-volatile % |
Acid value mgKOH/g |
Solvent | Hydroxyl value |
| Acrylic copolymer | Clear | ≤1 | 1.0-1.8 | 70±2 | 6-10 | BAC/XYL | 110 |
4. Compatibility and solubility
| XYL | + | BCS | + |
| TYL | + | CAC | + |
| BAC | + | CYC | + |
| PMA | + | NBA | + |
Remark:+ show soluble in/compatible in
5. Reference formula
| Two component (cover light varnish) | Diluent | ||
| (A component) | |||
| SE6783 | 70.0 | XYL | 40 |
| BYK-333 | 0.3 | TOL | 5 |
| 10%sn | 0.5 | BAC | 25 |
| BYK-052 | 0.1 | CAC | 15 |
| XYL | 10.0 | PMA | 15 |
| BAC | 19.2 | ||
| (B component) Bayer N3390 | |||
A component: B component: diluent=100: 22: 80~100
6. Process conditions
▲ Baking condition: (1) 65℃ x 60min, place 24hours for test
(2) Air drying
▲ Substrate: Sand plate tin
7. Test technical index
| Test Item | Test Method | Reference Standard | Test Standard |
Test Result (reference value) |
| Surface drying | Blow cotton ball method | ------ | Not stick cotton ball | 38min(25μm) |
| Hard drying | Finger pressing method | ------ | No finger print | 24h(25μm) |
| 8h hardness | Pencil scratch | GB/T6739-96 | ----- | <HB |
| 24h hardness | Pencil scratch | GB/T6739-96 | ----- | HB |
| Gloss | 60 degree | GB/T9754-88 | ≥90 | 110 |
| Hardness | Pencil scratch | GB/T6739-96 | ≥2H | 2H |
| Impact | Impact method | GB/T1732-93 | ≥30kg.cm | 50cm(25μm) |
| Flexibility | Bending method | GB/T1731-93 | ≤2mm | 1mm |
| Adhesion | The case method | GB/T9286-98 | 100% | 100% |
| Fullness | Visual method | ----- | Excellent fullness, good brightness | Excellent |
| Levelling property | Visual method | ----- | Flat and smooth, no shrinkage hole | Qualified |
| Ageing resistance | QUV machine | ----- |
800h no color change, not falling off, gloss loss rate≤1% |
Qualified |
| Acid resistance | Soak method | GB/T9274-88 | 10%H2SO4 72h not bubbling, not falling off, no color change | Qualified |
| Alkali resistance | Soak method | GB/T9274-88 | 5%NaOH 48h not bubbling, not falling off, no color change | Qualified |
8. Safe storage and shelf life
1. Stored in cool and ventilation place, keep far away from heat and fire resources, keep the container closed.
2. From production date, shelf life is 12months.
9. Packing specifications
200kg/pail (new metal pail)
10. Safety
This product contains solvent, must do safeguard procedure, handle carefully, avoid contact with the skins and eyes, for other details, please refer to MSDS of this product.
Company Details
Business Type:
Manufacturer,Importer,Exporter,Trading Company
Year Established:
2010
Employee Number:
10~50
Ecer Certification：
Verified Supplier
Established in 2010, Xiamen WangQin Chemical Technology is a professional corporation specializing in researching, developing manufacturer for different resin products. With a staff of 50 people, WangQin has been equipped with advanced manufacturing facilities and a full range of product testing equ... Established in 2010, Xiamen WangQin Chemical Technology is a professional corporation specializing in researching, developing manufacturer for different resin products. With a staff of 50 people, WangQin has been equipped with advanced manufacturing facilities and a full range of product testing equ...
Get in touch with us
Leave a Message, we will call you back quickly!