WUXI WANLI ADHESION MATERIALS CO., LTD.
| Payment Terms | L/C, T/T |
| Delivery Time | 5-8 work days |
| Packaging Details | 400 ml/Tube, 23L/Barrel, 195L/Barrel |
| performance | Component A: UH®-3005 A/ Component B:UH®-3005 B |
| Fundamentals of Chemistry | Component A: Polyol/ Component B: Isocyanate |
| colour(Before mixing） | Component A: black / Component B: canary yellow |
| colour(After mixing） | black |
| Curing mechanism | Addition polymerization |
| Density（ kg/l）(Before mixing） | Component A: 1.44 / Component B: 1.33 |
| Density（ kg/l）(After mixing） | 1.385 |
| Mixing ratio (A: B volume ratio) | 100 : 100 |
| Mixing ratio (A: B weight ratio) | 100 : 92.5 |
| Viscosity (brookfleld 7# rotor 10rpm25 ℃) | Component A: about 30000CPS / Component B: about 20000CPS |
| Applicable period (min) | 35A |
| Shore D hardness (ASTM D2240) | 60 |
| Tensile strength (ASTM D638 MPa) | 10 |
| Thermal conductivity (ASTM e1461 w/ (m · K)) | 0.5 |
| Elongation at break (ASTM D638) | 5-10 % |
| Shear strength (ASTM d1002 aluminum 3003- aluminum 3003 MPa) | 14.6 |
| working temperature | -40 – 80 °C |
| Brand Name | WANLI-ADHESION |
| Model Number | UH®-3005 |
| Certification | ISO9001 ISO14001 IATF16949 |
| Place of Origin | CHINA |
View Detail Information
Explore similar products
Distinctive 2KPU-802 Polyurethane Adhesive 700 MPa.S
Product Specification
| Payment Terms | L/C, T/T | Delivery Time | 5-8 work days |
| Packaging Details | 400 ml/Tube, 23L/Barrel, 195L/Barrel | performance | Component A: UH®-3005 A/ Component B:UH®-3005 B |
| Fundamentals of Chemistry | Component A: Polyol/ Component B: Isocyanate | colour(Before mixing） | Component A: black / Component B: canary yellow |
| colour(After mixing） | black | Curing mechanism | Addition polymerization |
| Density（ kg/l）(Before mixing） | Component A: 1.44 / Component B: 1.33 | Density（ kg/l）(After mixing） | 1.385 |
| Mixing ratio (A: B volume ratio) | 100 : 100 | Mixing ratio (A: B weight ratio) | 100 : 92.5 |
| Viscosity (brookfleld 7# rotor 10rpm25 ℃) | Component A: about 30000CPS / Component B: about 20000CPS | Applicable period (min) | 35A |
| Shore D hardness (ASTM D2240) | 60 | Tensile strength (ASTM D638 MPa) | 10 |
| Thermal conductivity (ASTM e1461 w/ (m · K)) | 0.5 | Elongation at break (ASTM D638) | 5-10 % |
| Shear strength (ASTM d1002 aluminum 3003- aluminum 3003 MPa) | 14.6 | working temperature | -40 – 80 °C |
| Brand Name | WANLI-ADHESION | Model Number | UH®-3005 |
| Certification | ISO9001 ISO14001 IATF16949 | Place of Origin | CHINA |
| High Light | black 2K Polyurethane Adhesive ，yellow 2K Polyurethane Adhesive ，curing 2k pu adhesive | ||
2K Polyurethane Adhesive UH®-3005
UH®-3005 is a two-component room temperature curing polyurethane adhesive. UH®-3005 is a semi-structural elastic adhesive, which can be bonded to a variety of substrates.
APPLICATION
UH®-3005 is designed for high strength bond bonding of a variety of substrates, including fiberglass, painted metal and plastics. This product is only for users with professional skills. In order to verify the bonding effect and the compatibility of the product with the material, tests should be carried out in advance on the actual substrate and environment.
| Spec | UH®-3005 A | UH®-3005 B |
| Appearance | Black(Before Mixing) | Yellow(Before Mixing) |
| Black(After Mixing) | ||
| Component | Polyol | Isocyanate |
| Curing Mechanism | Addition Polymerization | |
| Density(Kg/l) | 1.44(Before Mixing) | 1.33(Before Mixing) |
| 1.385(After Mixing) | ||
| Mixing Ratio | A:B(Volume Ratio)=100:100 | |
| A:B(Weight Ratio)=100:92.5 | ||
| Viscosity | About 30000CPS | About 20000CPS |
| (Brookfleld 7# Rotor 10rpm25℃) | ||
| Applicable Period (min) | 35A | |
| Shore D Hardness | 60(ASTM D2240) | |
| Tensile Strength | 10(ASTM D638 MPa) | |
| Thermal Conductivity | 0.5(ASTM E1461 W/ (m · K)) | |
| Elongation At Break | 5~10%(ASTM D638) | |
| Shear Strength | 14.6(ASTM D1002 Aluminum 3003- Aluminum 3003 MPa) | |
| Working Temperature | -40 – 80 °C | |
| Shelf Life | 6 Months | |
| Package | 400 ml/Tube, 23L/Barrel, 195L/Barrel | |
FEATURE
Good construction performance
Long operating time
High strength
high elasticity
excellent resistance to dynamic loads
Curing Mechanism
UH ®- 3005 is cured by a two-component chemical reaction.
High temperature can accelerate the curing speed, while low temperature will slow down the curing speed.
Chemical Resistance
If it is used in thermal environment or chemical environment, we suggest to carry out relevant project test, please contact wanli bonding technology department.
Company Details
Business Type:
Manufacturer
Year Established:
1995
Employee Number:
100~500
Ecer Certification：
Verified Supplier
WUXI WANLI ADHESION MATERIALS CO., LTD. was established in 1995 with a registered capital of 20.91 million yuan. It is located in Wuxi High-tech Development Zone,Jiangsu Province. It is a professional manufacturer of PUR hot melt adhesive, two-components PU adhesive, EVA hot melt adhesive, hot-melt ... WUXI WANLI ADHESION MATERIALS CO., LTD. was established in 1995 with a registered capital of 20.91 million yuan. It is located in Wuxi High-tech Development Zone,Jiangsu Province. It is a professional manufacturer of PUR hot melt adhesive, two-components PU adhesive, EVA hot melt adhesive, hot-melt ...
Get in touch with us
Leave a Message, we will call you back quickly!