| Material | Alloy steel |
| Process | Cold drawn |
| Treatment | hardened |
| Surface | Black, peeled |
| Shape | Round |
| Length | Cut to length on request |
| Brand Name | VANFORGE |
| Certification | ISO9001, ISO10012, ISO14001, OHSAS18001, ABS, BV, DNV, Lloyd, NK |
| Place of Origin | China |
View Detail Information
Explore similar products
Bearing Cold Drawn 52100 Chrome Steel High Carbon Alloy Annealed Treatment
AISI 52100 High Carbon Steel , Cold Bending Steel Rod For Aircraft Parts
AISI 52100 Cold Drawn Hardened Alloy Steel Round Bar High Mechanical For Bearing
Quenched AISI 52100 Bearing Steel , 52100 Alloy Steel High Mechanical
Product Specification
| Payment Terms | L/C, T/T | Supply Ability | 5000 metric tons per month |
| Delivery Time | 60 days | Packaging Details | Seaworthy package for export |
| Material | Alloy steel | Process | Cold drawn |
| Treatment | hardened | Surface | Black, peeled |
| Shape | Round | Length | Cut to length on request |
| Brand Name | VANFORGE | Certification | ISO9001, ISO10012, ISO14001, OHSAS18001, ABS, BV, DNV, Lloyd, NK |
| Place of Origin | China | ||
| High Light | cold rolled steel bar ，cold bending steel rod | ||
SAE 52100 cold worked hardened alloy steel round bar
SAE 52100 Steel is a steel high carbon content, linked to chromium, used for processing when you want to achieve high hardness after hardening, between 62-66 HRC. It is a hardenable steel in oil.
Chemical Composition – C (0.98 – 1.10), Si (0.15-0.35), Mn (0.25-0.45), Cr (1.30-1.60)
Supply conditions – Supplied with maximum hardness of 250HB
APPLICATIONS
It is generally used components in the bearing manufacturing industry.
FORGING
ANSI 52100 steel should be held at a minimum temperature of 925 ºC and a maximum of 1150 ºC.
HEAT TREATMENT
Annealing: For its high carbon content of the steel 52100 must undergo spheroidizing annealing to optimize its machinability. The spheroidization is performed at around 750 ° C for times ranging between 15 and 20 hours. Cool the oven.
Standardization: The treatment should be done at the temperature of 870 – 890ºC for at least 1 hour for every 25 mm. Cool air. In special cases can use forced air.
Hardening: The austenitizing tempering must be carried out between 840 – 850 ° C, maintaining the time necessary to homogenize the temperature in cross section and cooling in oil.
Tempering: It must be done immediately after hardening when the temperature reaches about 70 ° C. The tempering is performed at temperatures between 120 – 200 ° C. The usual tempering temperature is around 150 ° C. Under these conditions there is no significant drop in hardness. In tempering at about 180 ° C the hardness can fall of 1 to 2 points HRC. The hardness variation as a function of the tempering temperature curve is shown in Arrangement below.
Product size range
Diameter: 40mm - 150mm
Length: on request
Production Process
Key clients
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter,Seller
Year Established:
1999
Total Annual:
120 million-150 million
Employee Number:
800~850
Ecer Certification：
Active Member
Suzhou Vanforge Metals Co., Ltd. was set up in April 1999 with a registered capital of 230 million Yuan in Zhangjiagang Bonded Area in Jiangsu Province of China. It has developed to be an important R&D and manufacture enterprise of high performance stainless steels and nickel alloys. &nb... Suzhou Vanforge Metals Co., Ltd. was set up in April 1999 with a registered capital of 230 million Yuan in Zhangjiagang Bonded Area in Jiangsu Province of China. It has developed to be an important R&D and manufacture enterprise of high performance stainless steels and nickel alloys. &nb...