BEIJING SINO STEEL ENGINEERING & EQUIPMENT CO., LTD.
| Delivery Time | 2-3months |
| Packaging Details | Stardard international package |
| Type | wide plate |
| Application | Continuous casting machine |
| Material | CuAg |
| Type 1 | narrow plate |
| Material 2 | Cu-Cr-Zr |
| Type 3 | slab |
| Brand Name | SEEC |
| Model Number | CCM |
| Certification | ISO |
| Place of Origin | China |
View Detail Information
Explore similar products
Convex shape and concave shape Cr Ni-Co Ni-Fe plating copper mould For
Copper Mould Plate For Low Carbon steel Continuous Casting Machine with ISO
Copper mould plate for high speed and high efficiency Rectangular and plate CCM
CuAg and Cu-Cr-Zr type slab Copper Mould Plate and bloom Copper Mould Plate and
Product Specification
| Delivery Time | 2-3months | Packaging Details | Stardard international package |
| Type | wide plate | Application | Continuous casting machine |
| Material | CuAg | Type 1 | narrow plate |
| Material 2 | Cu-Cr-Zr | Type 3 | slab |
| Brand Name | SEEC | Model Number | CCM |
| Certification | ISO | Place of Origin | China |
| High Light | patterned copper sheet ，carbon steel plate | ||
Copper mould plate H-beam 700-1016mm x 280-1000mm Length x Width
Our specialized know-how, quality control and service enable us to satisfy the market’s changing requirements. Concentrating on adaptability to the improvement of continuous casting technology with continuously ongoing research and development word, BEIJING SINO STEEL is providing optimal solutions to your moulds.
Reference Working Life
Less than 2000 mm X180mm (billet dimension):25000~30000 tons/each coating
More than 2000 MM X180MM (billet dimension):80000~120000tons/each coating
Less than 2000 mm X180mm (billet dimension):30000~40000 tons/each coating
More than 2000 MM X180MM (billet dimension):100000~150000tons/each coating
Note: It can be remilled and recoated for 3~5 times.
China Market Share: 20~30%
| Material | Chemical Composition | Mechanical Properties | Electric Conductivity (%IACS) | ||||
| Cu (%) | Others (%) | Tensile Strength σ b (N/mm2) | Yield Strength σ 0.2 (N/mm2) | Elongation δ (%) | Hardness (HB) | ||
| E-Cu | ＞99.90 | 200 | 40 | 40 | 45 | 98 | |
| SF-Cu | ＞99.85 | P0.015-0.040 | 240-310 | 190-250 | 25-10 | 80-95 | 85 |
| CuAg | ＞99.50 | Ag0.08-0.12 | 240-310 | 200-225 | 16-10 | 110-125 | 95 |
| Cu-Cr-Zr | ＞98.0 | Cr0.3-1.2 Zr0.08-0.3 | 375-445 | 280-355 | 20-13 | 115-130 | 80 |
| Material | CuAg, Cu-Cr-Zr |
| Design | H-beam |
| Rectangular | |
| Size | H-beam: 700-1016x280-1000 (LxW) Wall thickness:35-310mm
Rectangular:Max 5000mm×3800mm (L x W) Wall thickness:30-75mm |
| Coating | Coating material: Cr, Ni-Co or Ni-Fe |
| Material | CuAg, Cu-Cr-Zr |
| Design | H-beam |
| Rectangular | |
| Size | H-beam: 700-1016x280-1000 (LxW) Wall thickness:35-310mm
Rectangular:Max 5000mm×3800mm (L x W) Wall thickness:30-75mm |
| Coating | Coating material: Cr, Ni-Co or Ni-Fe |
| ltem | Temp | Unit | Material | ||
| CuDHP | CuAg0.1 | CuCrZr | |||
| Chemical Composition | |||||
| Cu 99.85 P0.015-0.040 | Cu 99.50 Ag0.08-0.12 | Cu 98 Cr 0.30-1.20 Zr 0.08-0.30 | |||
| Physical properties | |||||
| Electical conductivity | 20 | %IACS | 85 | 95 | 80 |
| Thermal conductivity | 20 | W/(m.K) | 340 | 375 | 330 |
| Coefficient of thermal expansion | 20-300 | 10^-6/K | 17.1 | 17.1 | 17.2 |
| Recrystallisation temperature | ℃ | 345 | 360 | 690 | |
| Modulus of elasticity | 20 | 10^3MPa | 120 | 123 | 126 |
| Melting point | ℃ | 1083 | 1083 | 1078 | |
| Specific gravity | g/cm3 | 8.9 | 8.9 | 8.9 | |
| Mechanical properties | |||||
| Ultimate tensile strength | 20 | Mpa | 240-310 | 240-310 | 375-445 |
| Ultimate tensile strength | 100 | Mpa | 190-270 | 230-270 | 365-425 |
| Ultimate tensile strength | 200 | Mpa | 140-190 | 205-240 | 365-410 |
| Ultimate tensile strength | 300 | Mpa | 175-210 | 335-375 | |
| Ultimate tensile strength | 400 | Mpa | 145-160 | 315-350 | |
| 0.2Yield point strength(Rp0.2) | 20 | Mpa | 190-250 | 200-225 | 280-355 |
| 0.2Yield point strength(Rp0.2) | 100 | Mpa | 185-260 | 195-240 | 270-345 |
| 0.2Yield point strength(Rp0.2) | 200 | Mpa | 180-225 | 260-330 | |
| 0.2Yield point strength(Rp0.2) | 300 | Mpa | 165-215 | 250-320 | |
| 0.2Yield point strength(Rp0.2) | 400 | Mpa | 130-145 | 240-290 | |
| Elongation(A5) | 20 | % | 25-10 | 16-10 | 20-13 |
| Hardness | 20 | HB | 80-95 | 110-125 | 115-130 |
| Note: TP2(GB/T5231-2001)Equivalent SF-Cu/DHP-Cu(DIN1787) TAg0.1(CuAg0.1)(GB/T5231-2001) Equivalent DPS-Cu(DIN1787) | |||||
Company Details
Business Type:
Manufacturer,Exporter
Year Established:
1997
Total Annual:
30000000-50000000
Employee Number:
500~10000
Ecer Certification：
Active Member
Beijing Sino Steel Engineering & Equipment Co., Ltd. is concentrating on developing of ferrous & non-ferrous making and Rolling technology, mainly. As one of the most experienced Chinese suppliers of complete line and components for steel and non-ferrous indu... Beijing Sino Steel Engineering & Equipment Co., Ltd. is concentrating on developing of ferrous & non-ferrous making and Rolling technology, mainly. As one of the most experienced Chinese suppliers of complete line and components for steel and non-ferrous indu...