SUZHOU HSF ELECTRONIC MATERIALS TECHNOLOGY CO., LTD.
| Payment Terms | T/T, L/C |
| Supply Ability | 80000kg per week |
| Delivery Time | within 10 days |
| Packaging Details | PE wrapping film + Bubble film + Wooden pallet (W.1100mm x L. 1100mm x H. 100mm), customized |
| Material | Mono-axially oriented polypropylene |
| Color | Customized |
| Halogen free | Yes |
| Thickness | 25- 100μm, customized |
| Width | ≤1400 ± 5mm |
| Core | 3" or 6" |
| Coating | Single or Double Side UV Cured Silicone Coating |
| Release Force | Customized |
| Subsequent Adhesion Rate | ≥75% |
| Length | Customized |
| Splice | ≤1 |
| Sample | A4 sheet for free |
| Brand Name | HSF |
| Place of Origin | China |
View Detail Information
Explore similar products
70 μm 80 μm MOPP Film Mono-Axially Oriented Polypropylene Release Film
≤ 200 μm Sky Blue Monoaxially Oriented Polypropylene (MOPP) Film for Electronic
85 μm MOPP Film Monoaxially Oriented Polypropylene Release Film in Green Blue
Mono Axially Oriented Polypropylene Single Side Silicone Release Film 85micron
Product Specification
| Payment Terms | T/T, L/C | Supply Ability | 80000kg per week |
| Delivery Time | within 10 days | Packaging Details | PE wrapping film + Bubble film + Wooden pallet (W.1100mm x L. 1100mm x H. 100mm), customized |
| Material | Mono-axially oriented polypropylene | Color | Customized |
| Halogen free | Yes | Thickness | 25- 100μm, customized |
| Width | ≤1400 ± 5mm | Core | 3" or 6" |
| Coating | Single or Double Side UV Cured Silicone Coating | Release Force | Customized |
| Subsequent Adhesion Rate | ≥75% | Length | Customized |
| Splice | ≤1 | Sample | A4 sheet for free |
| Brand Name | HSF | Place of Origin | China |
| High Light | Color customized MOPP Film ，Mono-axially oriented polypropylene Release Film ，Transparency MOPP Film | ||
Mono-axially oriented polypropylene Release Film, Color customized, High mechanical strength, Transparency
| S/N | Inspection Item | Measure Unit | Executive Standard | Typical Value | |
| 1 | Appearance Quality | - | No creases, damages, pollution or rough burrs | ok | |
| 2 | Density | g/cm³ | - | 0.9 | |
| 3 | Thickness | mm | GB/T 6673-2001 | 0.025-0.100 | |
| 4 | Thickness Deviation | % | GB/T 6673-2001 | ≤3 | |
| 5 | Tensile Strength | MD | Mpa | GB/T 1040.3-2006 | ≥280 |
| 6 | Elongation @ break | MD | % | GB/T 1040.3-2006 | ≥40 |
| TD | % | GB/T 1040.3-2006 | ≥500 | ||
| 7 | Surface Tension (Single / Double) | mN/m | GB/T 14216-2008 | ≥42 | |
| 8 | Shrinkage (120℃/3min) | MD | % | GB/T 10003-2008 | ≤5 |
| TD | % | ≤0 | |||
MOPP is the abbreviation of Mono-axially Oriented Polypropylene.
It has a significant high tensile strength in the mechanical direction,
the longitudinal strength and longitudinal crack resistance are greatly improved, and it has good kink.
It has the advantages of light weight, transparency, non-toxicity, moisture resistance and high mechanical strength,
and is widely used in packaging films, cigarette film pulling wires, etc., and is widely used as composite film substrate,
self-adhesive tapes, cable tapes, tear tapes, silicone-coated base films, strapping tapes (such as wrapping steel),
article labels, tire lining applications, etc.
At present, the most commonly used production method of MOPP film in the industry is the main casting method.
In the casting method, the prepared plastic is firstly plasticized and melted through an co-extruder.
It is extruded through a T-shaped structure forming die and cast in a sheet shape onto the roller surface of a smoothly
rotating cooling roller.
The film is cooled and shaped on the cooling roller, and then the product is rolled up after being pulled and trimmed.
The products produced by the casting method (flat film method) have superior performance and mature equipment.
It has high production efficiency and is suitable for mass production, and is currently widely used by enterprises.
Company Details
Business Type:
Manufacturer,Importer,Exporter
Year Established:
2018
Total Annual:
15million-18million
Employee Number:
50~100
Ecer Certification：
Verified Supplier
... ...
Get in touch with us
Leave a Message, we will call you back quickly!