HLS Coatings （Shanghai）Co.Ltd
| Supply Ability | 200 Tons Per Day |
| Delivery Time | 30-60 Days |
| Packaging Details | 50kg、60 kg、200kg、1000kg packaging barrels |
| main ingredients | carbon black, kaolin |
| Application field | car covers |
| Performance | film smooth |
| Cooperation case | ANHUI Xin hong traffic， |
| Brand Name | HAOLISEN |
| Model Number | HS-6060LB/HS-2668G |
| Certification | IATF16949 , ISO9001 |
| Place of Origin | Shanghai China （Mainland） |
View Detail Information
Explore similar products
Two Component E Coating Car Body Painting Grey Color Scratch Resistant
Non - Inflammable Cationic Epoxy Electrocoat , Edpaint For Car Protective
Stone Resistant E Coating Car Body Paint With Anti Rust Pigment Ingredients
High Performance Electrophoresis Paint , Electrocoating Anti Rust Coating For
Product Specification
| Supply Ability | 200 Tons Per Day | Delivery Time | 30-60 Days |
| Packaging Details | 50kg、60 kg、200kg、1000kg packaging barrels | main ingredients | carbon black, kaolin |
| Application field | car covers | Performance | film smooth |
| Cooperation case | ANHUI Xin hong traffic， | Brand Name | HAOLISEN |
| Model Number | HS-6060LB/HS-2668G | Certification | IATF16949 , ISO9001 |
| Place of Origin | Shanghai China （Mainland） | ||
| High Light | cathodic electrocoating ，car paint coating | ||
Solution for the car covers electrophoresis paint.
Product Introduction
| HS-6060LB/HS-2668G Gray Cationic Epoxy Electrocoat for auto is a new generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd. It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin,meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc. |
This product features shown below:
| Coating fullness of good, better substrate hiding . |
| Strong anti-corrosion properties, good salt spray resistance workpiece edge. |
| The appearance of the coating is flat, delicate, smooth. |
| Good stability of bath can adaptable for a longer updating cycle. |
| Excellent leveling coating,good bonding force and compatibility with plastic powder. |
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 1000.00-1250.00
Paste 250.00
DI water 1500.00
Total 2750.00
⑵ Ripening conditions
| Sample quantity | 3000～4000g |
| Container | 4L (Diameter 16cm) |
| Tank temperature | 28-30 ℃ |
| Time | 24～48Hr |
| Mixed conditions | impeller diameter 8cm (speed 200rpm) |
(3) Coating conditions
| Experimental panel | phosphated cold-rolled steel plate |
| Tank temperature | 28-35℃ |
| Pole ratio | A/C = 1/2 ~ 1/4 |
| Distance of electrodes | 15cm |
| ED time | For full immersing 1-3 minutes ( 20 seconds soft start) |
| Baking conditions | (175-185)℃×(20-30)min (Keeping temperature of parts coated) |
Product film performance
| Project | Indicator | Test standard | |
| Appearance | Normal / abnormal | Normal | Ocular estimate |
| Hardness | ≥ | 2H | GB/T 6739 |
| Cup drawing | mm ,≥ | 6 | GB/T 9753 |
| Adhesion | Level | 0 | GB/T 9286 |
| Flexibility | mm | 1 | GB/T 1731 |
| Impact | kg·cm | 50 | GB/T 1732 |
| Gloss | 60 | 50-80 | GB/T 9754 |
| Water resistance | h,(23±2)℃,≥ | 240 | GB/T 1733 |
| Acid resistance | h,(50g/L H2SO4),≥ | 72 | GB/T 9274 |
| Alkali resistance | h,(50g/L NaOH),≥ | 48 | GB/T 9274 |
| *Salt spray resistance | h,(film thickness ≥ 20μm) ,≥ | 1000 | GB/T 1771 |
* Note: The substrate use the Bonder standard phosphating steel panel, crossed out unidirectional expansion eclipse ≤ 2mm.
Customer production site
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2003
Total Annual:
100million-120million
Employee Number:
315~360
Ecer Certification：
Verified Supplier
Since its foundation in November 2003, HAOLISEN has been adhering to the vision of “Advocator and Innovator of Waterborne Coating Solutions” and committed to the development and production of industrial electrophoretic coatings by investing lots of human, material, energy and financial r... Since its foundation in November 2003, HAOLISEN has been adhering to the vision of “Advocator and Innovator of Waterborne Coating Solutions” and committed to the development and production of industrial electrophoretic coatings by investing lots of human, material, energy and financial r...