HLS Coatings （Shanghai）Co.Ltd
| Supply Ability | 200 Tons Per Day |
| Delivery Time | 30-60 Days |
| Packaging Details | 50kg、60 kg、200kg、1000kg packaging barrels |
| main ingredients | organic acid |
| Application field | oil-radiator |
| Performance | Combustion odour |
| Cooperation case | GREE,Midea，Singfun |
| Brand Name | HAOLISEN |
| Model Number | HS-6500LB/HS-6500 |
| Certification | IATF16949 , ISO9001 |
| Place of Origin | Shanghai China （Mainland） |
View Detail Information
Explore similar products
Epoxy Acrylate Modified Ced Coating , Electrophoretic Painting For Motorcycle
Black Cationic Epoxy Electrocoat Low Temperature Cure For Compressor
Oil Resistant Cathodic Electrodeposition Paint For Household Kitchen Electric
Cathodic Electrodeposition Coating , Ced Automotive Paints And Coatings
Product Specification
| Supply Ability | 200 Tons Per Day | Delivery Time | 30-60 Days |
| Packaging Details | 50kg、60 kg、200kg、1000kg packaging barrels | main ingredients | organic acid |
| Application field | oil-radiator | Performance | Combustion odour |
| Cooperation case | GREE,Midea，Singfun | Brand Name | HAOLISEN |
| Model Number | HS-6500LB/HS-6500 | Certification | IATF16949 , ISO9001 |
| Place of Origin | Shanghai China （Mainland） | ||
| High Light | cathodic epoxy electrocoat ，cathodic electrodeposition coating | ||
Solution for oil-radiator electrodeposition coating
Product Introduction
HS-6500LB/HS-6500 White epoxy acrylic cathodic electrophoretic coating for auto is the 9th generation electrophoretic coating researched and developed by HLS Paint (Shanghai) Co., Ltd., and get the national invention patent and the Shanghai science and technology commission of high-tech transformation project.
It represents modern technology of cathodic electrophoretic coating that is environment-friendly with high property and low cost. Such coating does not contain heavy metal like lead, tin, cadmium and mercury etc. It is a two-component, water-dispersed resin. The coating that does not contain tin element meet the latest environ-mental regulations of European Union, North America, Japan and other requirements in advance, which is the inevitable trend of future environ-mental coating and low cost; meanwhile, it took in features of previous products, and can adapt galvanized steel sheet perfectly, almost can be applied to foundation coating of all metal, such as: cold and hot rolled steel sheet, galvanized steel sheet, aluminum products, zinc-aluminum alloy sheet and stainless steel sheet etc.
This product features shown below:
|
High throwing power, good internal and external uniformity.
|
|
Simple control of bath and wide operation range is suitable for the operation specification and site equipment for different customers.
|
|
Low curing temperature, coating yellow degeneration resistance is good, suitable for electrodeposition primer, and then to spray or paint coating process, such as: oil heater, radiator, heater, lamps and lanterns, machinery, home appliances and hardware products and other industries.
|
Main ingredients:
Pigment: titanium dioxide, kaolin,antirust pigment
Neutralizing agent: organic acid
Additives: surface active agent, prevent shrinkage cavity agent,resistance to yellowing agent
Bath on site management project:
Good bath data and coating quality, from the strict parameters management and maintenance of equipment, production line according to its own reality time situation, can have different management project and specifications, recommend the construction parameters see the table below for reference:
| Classification | Project | Control Data | Testing frequency | |
| New bath | Anolyte | |||
| Electrophoresis tank | Ratio | 1:3-4 | -- | |
| Ripening time | 24-48 | -- | ||
| Solid ( 120 ℃ /1h ,% ) | 12±2 | -- | once a day | |
| PH | 5.3-5.8 | 2.0-3.5 | once a day | |
| Conductivity ( μs/cm ) | 1000±400 | 1000±500 | once a day | |
| P/B | 0.25-0.35 | once a week | ||
| Solvent content (%) | 0.8-1.5 | once a week | ||
| Liquid level Fall head (cm ) | 10-15 | once a day | ||
| ED voltage( V ) | 0-300 | once a day | ||
| Break voltage ( V ) | ≥350 | once a week | ||
| Bath temperature ( ℃ ) | 30±2 | once a day | ||
| ED time( S ) | 60~180 | once a day | ||
| UF － 1 Tank | Solid content (%) | ≤2.0 | once a day | |
| UF － 2 Tank | Solid content (%) | ≤0.8 | once a day | |
| Baking furnace | Provisions furnace temperature( ℃ ) | 145-165 | once a day | |
| Curing conditions | Drying temperature | (140-160) ℃ ×(20-30)min (With content holding tim |
once a day | |
Filling tank proportion and method
⑴ Bath preparation
Ratio:
Resin 1020.00
Paste 300.00
DI water 3280.00
Total 3 4600.00
⑵ Ripening conditions
Sample quantity: 4600g
Container: 5L (Diameter 16cm)
Tank temperature:28-30 ℃
Time: 24～48Hr
Mixed conditions: impeller diameter 8cm (speed 200rpm)
(3) Coating conditions
Experimental panel: phosphated cold-rolled steel plate
Tank temperature: 30±2℃
Pole ratio: A/C = 1/2 ~ 1/4
Distance of electrodes: 15cm
ED time: For full immersing 1-3 minutes ( 20 seconds soft start)
Baking conditions:(140-160)℃×(20-30)min (Keeping temperature of parts coated)
Company Details
Business Type:
Manufacturer,Seller
Year Established:
2003
Total Annual:
100million-120million
Employee Number:
315~360
Ecer Certification：
Verified Supplier
Since its foundation in November 2003, HAOLISEN has been adhering to the vision of “Advocator and Innovator of Waterborne Coating Solutions” and committed to the development and production of industrial electrophoretic coatings by investing lots of human, material, energy and financial r... Since its foundation in November 2003, HAOLISEN has been adhering to the vision of “Advocator and Innovator of Waterborne Coating Solutions” and committed to the development and production of industrial electrophoretic coatings by investing lots of human, material, energy and financial r...
Get in touch with us
Leave a Message, we will call you back quickly!