Success Dental Company
| Payment Terms | Western Union, L/C, T/T |
| Supply Ability | 100 + kg + per day |
| Delivery Time | 5-8 working days |
| Packaging Details | bottle or paper box |
| Density | 8.5g/cm3 |
| Elongation | 5% |
| Melting range | 1250-1300C |
| Vickers hardness | 360HV10 |
| Co | 60% |
| Cr | 31% |
| Mo | 5.6% |
| Modulus of elasticity | 190GPa |
| Brand Name | Willett |
| Model Number | CF-s |
| Place of Origin | China |
View Detail Information
Explore similar products
Partial Denture Cobalt Based Alloys , Base Metal Casting Alloys Smooth Surface
Metal Alloy Used For Dental Fillings , High Temperature Alloys Good Toughness
Nickel Based Non Precious Dental Alloys 25.2 - 27.3% Chrome No Cytotoxic
Eco Friendly Base Metal Alloys In Dentistry , Copper Cobalt Alloy No Beryllium
Product Specification
| Payment Terms | Western Union, L/C, T/T | Supply Ability | 100 + kg + per day |
| Delivery Time | 5-8 working days | Packaging Details | bottle or paper box |
| Density | 8.5g/cm3 | Elongation | 5% |
| Melting range | 1250-1300C | Vickers hardness | 360HV10 |
| Co | 60% | Cr | 31% |
| Mo | 5.6% | Modulus of elasticity | 190GPa |
| Brand Name | Willett | Model Number | CF-s |
| Place of Origin | China | ||
| High Light | ni cr alloy ，high temperature alloys | ||
Dental Non Precious Dental Alloys made with Cobalt Chrome for framework in shot shape
With or without label in irregular shapes
Advantages:
(1). Superior mechanical performance castability, toughness
(2). Corrosion resistance , wear resistance , high intensity , high hardness, stays in shape
(3). Nickle-free & beryllium-free, great biocompatibility
Properties:
Melting Point: 1250-1300 ℃
Density : 8.5g/cm3
Hardness: 360HV10
Modulus of elasticity: 190GPa
Elongation: 5%
Composition:
| Co | Cr | Mo | W | Others |
| 60-63 | 27-29 | 5-6 | 4-6 | ≤0.5 |
FAQ:
What is the perfect temperature to obtain the best result when casting?
The casting temperature should always maintain 100~150℃ higher than liquidus temperature.
What is the perfect timing to obtain the best result when casting?
While casting Nickel Chrome alloys that don't contain Beryllium, the surface of the melting alloys will appear a layer of shadow. Once the shadow disappears and the edges of the alloy have become rounded (melted until it becomes a sphere shape is not necessary) will be the best timing for casting. Perfect timing for casting Cobalt Chrome alloy is to heat it till the surface membrane perforated and a spark of bright light start to appear.
Cobalt Chrome casting piece is incomplete, what are the causes?
1. Casting ring is not heated evenly: While casting Cobalt alloys, casting ring must heat up gradually and slowly before reaches 300℃. Let it sit in the oven in between 300℃ and 600℃ for 10-30 minutes. Once it heats up to the desired temperature, maintain the same temperature for at least 30 minutes before casting.
2. Casting temperature is below/above alloy's requirement.
3. Strub designed improperly: For example, Strub is too narrow. We strongly recommend the Strub diameter consist of 5mm or more.
4. The amount of alloy is not enough for the casting piece or the centrifugal force of casting pressure is not enough.
5. Casting piece has not avoided the heat center.
Company Details
Business Type:
Manufacturer,Trading Company
Year Established:
1978
Employee Number:
100~150
Ecer Certification：
Active Member
Success Dental Company provides dental products from laboratory use to clinical use. The company is based in Hong Kong where is known as the free trade city. Our factory is located in Dongguan. The company was found in the 1970s and has always been the top company among all the competitors. After se... Success Dental Company provides dental products from laboratory use to clinical use. The company is based in Hong Kong where is known as the free trade city. Our factory is located in Dongguan. The company was found in the 1970s and has always been the top company among all the competitors. After se...
Get in touch with us
Leave a Message, we will call you back quickly!