MKarte Material Technology (Tianjin) Limited
| Payment Terms | L/C, T/T, Western Union, MoneyGram |
| Supply Ability | 20 million square meters or 5 million tons per month |
| Delivery Time | 10-15 working days |
| Packaging Details | by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet. |
| Normal thickness | 0.04-0.10mm |
| Package method | by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet. |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
| Vicat softening point | 72±2 ℃ |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Brand Name | MK |
| Model Number | MCO-W |
| Place of Origin | China |
View Detail Information
Explore similar products
Strong Adhesion Level PVC Coated Overlay
strong adhesion level PVC Coated Overlay in sheet or roll ( 0.06-1.0mm thickness
Long Life PVC Overlay Sheet Clean And Flatness Surface With Excellent Peeling
Offset PVC Sheet Printing PVC Coated Overlay With Yellowing Resistance
Product Specification
| Payment Terms | L/C, T/T, Western Union, MoneyGram | Supply Ability | 20 million square meters or 5 million tons per month |
| Delivery Time | 10-15 working days | Packaging Details | by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet. |
| Normal thickness | 0.04-0.10mm | Package method | by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet. |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink | Vicat softening point | 72±2 ℃ |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm | Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Brand Name | MK | Model Number | MCO-W |
| Place of Origin | China | ||
| High Light | transparent pvc coated overlay ，pvc coated overlay transparent ，1.0mm pvc coated overlay | ||
PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness
1. PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness- Introduction
PVC Coated Overlay MCO-W model is suitable for laminating with most PVC sheets printed by various printers. It features high adhesion, no color change and deformation.
It is applicable to almost all sheets printed by various ink. It features excellent peeling strength and long aging time.
2. PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness- Parameters:
| Size | in reel or sheet, A4, A3 or as per customer requirements |
| Normal thickness | 0.04,0.05,0.06,0.08,0.10mm |
| Color | transparent with one-side glue coating. |
| Package method | by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet. |
| Storage condition | Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight. |
3.PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness- Technical Parameters:
| Item | Parameters |
| Vicat softening point | 72±2 ℃ |
| Heating Shrinkage ratio | ≤10 % |
| Tensile Strength | ≥40 MPa |
| Normal thickness in mm | 0.04,0.05,0.06,0.08,0.10 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
4.PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness- Application
| Item | Parameters | |
| Vicat (℃) | 72±2 ℃ | |
| Shrinkage (%) | ≤10% | |
| Tensile Strength (MPa) | MD | ≥40 |
| TD | ≥35 | |
| Roughness (μm) | Ra | 0.5~1.8 |
| Rz | 3~9 | |
| Thickness (mm) | 0.04~0.1 | |
Product Category and Laminating Condition:
| Product Category | MCO-W | ||||||
| Application | ID Card,Social Security Card,Bank Card,etc | Bank Card,Shopping Card,etc | Membership Card,Commercial Card,etc | ||||
| Suggested Laminating Condition | Laminating Unit | Heat Laminating | Cool Laminating | Heat Laminating | Cool Laminating | Heat Laminating | Cool Laminating |
| Temp | 130~150℃ | ≤25℃ | 130~150℃ | ≤25℃ | 135~155℃ | ≤25℃ | |
| Time | 25min | 15 min | 25min | 15 min | 25min | 15 min | |
| Pressure | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa | ≥5MPa | |
5.PVC Coated Overlay MCO-W strong adhesion level 0.04-1.0mm thickness- Packing and Storage
Package method: by reel or 500 sheets per bag/4-8 bags per paper carton, or as per customer requirements. All the cartons are firmly piled up and fixed on the solid plywood pallet.
Storage condition: Sealed, moisture-proof, room temperature under 40℃, Keep it horizontally, avoid heavy pressing and direct sunlight.
Company Details
Business Type:
Manufacturer,Distributor/Wholesaler,Exporter,Seller
Year Established:
2016
Total Annual:
5 million-10 million
Employee Number:
50~100
Ecer Certification：
Verified Supplier
MKarte Material Technology (Tianjin) Limited (hereinafter referred as MMT) has been specializing in supplying all-round material solutions for card production industry worldwide. Our products are widely used in the card body production of such cards as EMV financial card, ID card, telecom cards, IC ... MKarte Material Technology (Tianjin) Limited (hereinafter referred as MMT) has been specializing in supplying all-round material solutions for card production industry worldwide. Our products are widely used in the card body production of such cards as EMV financial card, ID card, telecom cards, IC ...