| Deflection | 19mm |
| Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa |
| Closed cell rate | 98% |
| Tensile modulus | 200Mpa |
| Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa |
| Shear strength | 2Mpa |
| Shear modulus | 63Mpa |
| Origin | China |
| Brand Name | Tasuns |
| Model Number | PMI Foam |
| Certification | CE, SGS, ISO |
| Place of Origin | Dongguan, China |
View Detail Information
Explore similar products
Polymethacrylimide PMI Foam Core Fine Holes 51HF 52 kg/m3
19mm PMI Core Carbon Composite Plate For Medical Component
Polymethacrylimide PMI Foam Core Density 110 For Sea Fishing
CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite
Product Specification
| Payment Terms | T/T, L/C | Supply Ability | 100cbm/week |
| Delivery Time | 7-10 days for sample | Packaging Details | Plywood |
| Deflection | 19mm | Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa | Closed cell rate | 98% |
| Tensile modulus | 200Mpa | Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa | Shear strength | 2Mpa |
| Shear modulus | 63Mpa | Origin | China |
| Brand Name | Tasuns | Model Number | PMI Foam |
| Certification | CE, SGS, ISO | Place of Origin | Dongguan, China |
| High Light | 19mm PMI Foam Core ，195Mpa PMI Foam Core ，polymethacrylimide foam Fishing Float | ||
PMI Core Rohacell 110 Foam For Fishing Float
Why PMI foam for fishing float?
1. Large buoyancy ratio.
2. The material draft is small.
3. The material density is uniform and stable.
4. The material is strong and durable.
5. Strong plasticity.
6. The low cost of raw materials, rapid forming and high yield are very suitable for factory production.
Tasuns PMI foam specification:
| Density (kg/m³) | Model | Mechanical properties at room temperature | ||||||||||
| Compressive strength | Compression modulus | Tensile Strength | Tensile modulus | Elongation at break | Shear strength | Shear modulus | Bending strength | Flexural modulus | Deflection | Closed cell rate | ||
| Mpa | Mpa | Mpa | Mpa | % | Mpa | Mpa | Mpa | Mpa | mm | % | ||
| Testing standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2008 | GB/T 8812.2-2007 | GB/T 10799-2008 | |||||||
| 32 | XK32 | 0.32 | 14 | 0.66 | 28 | 3.8 | 0.28 | 7.6 | 0.86 | 31 | 22 | 99 |
| CX30 | 0.42 | 20 | 0.56 | 39 | 0.69 | — | — | 1 | 31 | 30 | — | |
| 40 | CK40 | 0.6 | 34 | 0.9 | 54 | 1.7 | 0.4 | 19 | 1.3 | 55 | 15 | — |
| CX40 | 0.72 | 29 | 1.2 | 51 | 3.4 | — | — | 1.7 | 58 | 33 | — | |
| 52 | CK52 | 0.9 | 41 | 1.2 | 73 | 1.9 | 0.73 | 27 | 1.6 | 70 | 19 | 99 |
| ZK52 | 0.9 | 51 | 1.3 | 81 | 1.2 | 1 | 26 | 1.5 | 65 | 15 | 97 | |
| XK52 | 1 | 43 | 1.5 | 77 | 3.1 | 0.9 | 24 | 2.1 | 76 | 22 | 99 | |
| 75 | CK72 | 1.4 | 59 | 1.8 | 101 | 2.3 | 1.2 | 40 | 2 | 92 | 13 | 99 |
| XK75 | 1.8 | 72 | 2.4 | 113 | 3.6 | 1.6 | 45 | 3.4 | 117 | 20 | 98 | |
| CX75 | 1.7 | 75 | 2.2 | 89 | 3.8 | 1.2 | 37 | 3.3 | 105 | 23 | — | |
| 110 | XK110 | 3.2 | 138 | 3.9 | 200 | 2.7 | 2 | 63 | 5.5 | 195 | 19 | 98 |
| CX110 | 2.2 | 93 | 3.3 | 160 | 3.6 | 2.2 | 63 | 4.5 | 143 | 21 | — | |
| 200 | XK200 | 8.5 | 317 | 7.5 | 410 | 2.4 | — | — | 13 | 449 | 22 | 99 |
Application for Tasun structrual foam:
PMI foam has been widely used in aviation, aerospace, military radar, maglev train, high-speed ship, automobile manufacturing, sports equipment, medical equipment, audio products and other fields.
Our workshop:
FAQ:
1. How can I get the reasonable price efficiently?
-Quantity, specification and 3D drawing will be helpful.
2. What file format are available for you to open?
-DWG, DXF, STP, IGS are available.
3. What is your payment term?
-T/T and Paypal are common, other methods could be discussed.
Company Details
Business Type:
Manufacturer
Year Established:
2006
Total Annual:
300-400
Employee Number:
70~80
Ecer Certification：
Verified Supplier
Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye... Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye...
Get in touch with us
Leave a Message, we will call you back quickly!