| Deflection | 19mm |
| Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa |
| Closed cell rate | 98% |
| Tensile modulus | 200Mpa |
| Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa |
| Shear strength | 2Mpa |
| Shear modulus | 63Mpa |
| Origin | China |
| Brand Name | Tasuns |
| Model Number | PMI Foam |
| Certification | CE, SGS, ISO |
| Place of Origin | Dongguan, China |
View Detail Information
Explore similar products
Polymethacrylimide PMI Foam Core Fine Holes 51HF 52 kg/m3
19mm PMI Core Carbon Composite Plate For Medical Component
Polymethacrylimide PMI Foam Core Density 110 For Sea Fishing
Fire Retardant Natural White PMI Foam Polymethacrylimide 110
Product Specification
| Payment Terms | T/T, L/C | Supply Ability | 100cbm/week |
| Delivery Time | 7-10 days for sample | Packaging Details | Plywood |
| Deflection | 19mm | Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa | Closed cell rate | 98% |
| Tensile modulus | 200Mpa | Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa | Shear strength | 2Mpa |
| Shear modulus | 63Mpa | Origin | China |
| Brand Name | Tasuns | Model Number | PMI Foam |
| Certification | CE, SGS, ISO | Place of Origin | Dongguan, China |
| High Light | CNC Machined pmi core ，19mm foam sandwich panels ，5.5Mpa pmi core | ||
CNC Machined PMI Core For Medical Equipment
Why use PMI foam for x-ray medial board?
PMI stands for polymethacrylimide. PMI foam cores are one of the strongest options for building Sandwich composite panels. For the same density, PMI foam cores offer some of the highest overall strengths and stiffnesses of foam cores. PMI foam cores have mainly been used in higher performance composite parts such as helicopter rotor blades, ailerons and stringer profiles in pressure bulkheads, high speed trains, UAVs, medical equipments, radome and antennas.
Tasuns PMI foam specification:
1) fine pores
2) coarse pores
3) ultra-fine pores.
| Density (kg/m³) | Model | Mechanical properties at room temperature | ||||||||||
| Compressive strength | Compression modulus | Tensile Strength | Tensile modulus | Elongation at break | Shear strength | Shear modulus | Bending strength | Flexural modulus | Deflection | Closed cell rate | ||
| Mpa | Mpa | Mpa | Mpa | % | Mpa | Mpa | Mpa | Mpa | mm | % | ||
| Testing standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2008 | GB/T 8812.2-2007 | GB/T 10799-2008 | |||||||
| 32 | XK32 | 0.32 | 14 | 0.66 | 28 | 3.8 | 0.28 | 7.6 | 0.86 | 31 | 22 | 99 |
| CX30 | 0.42 | 20 | 0.56 | 39 | 0.69 | — | — | 1 | 31 | 30 | — | |
| 40 | CK40 | 0.6 | 34 | 0.9 | 54 | 1.7 | 0.4 | 19 | 1.3 | 55 | 15 | — |
| CX40 | 0.72 | 29 | 1.2 | 51 | 3.4 | — | — | 1.7 | 58 | 33 | — | |
| 52 | CK52 | 0.9 | 41 | 1.2 | 73 | 1.9 | 0.73 | 27 | 1.6 | 70 | 19 | 99 |
| ZK52 | 0.9 | 51 | 1.3 | 81 | 1.2 | 1 | 26 | 1.5 | 65 | 15 | 97 | |
| XK52 | 1 | 43 | 1.5 | 77 | 3.1 | 0.9 | 24 | 2.1 | 76 | 22 | 99 | |
| 75 | CK72 | 1.4 | 59 | 1.8 | 101 | 2.3 | 1.2 | 40 | 2 | 92 | 13 | 99 |
| XK75 | 1.8 | 72 | 2.4 | 113 | 3.6 | 1.6 | 45 | 3.4 | 117 | 20 | 98 | |
| CX75 | 1.7 | 75 | 2.2 | 89 | 3.8 | 1.2 | 37 | 3.3 | 105 | 23 | — | |
| 110 | XK110 | 3.2 | 138 | 3.9 | 200 | 2.7 | 2 | 63 | 5.5 | 195 | 19 | 98 |
| CX110 | 2.2 | 93 | 3.3 | 160 | 3.6 | 2.2 | 63 | 4.5 | 143 | 21 | — | |
| 200 | XK200 | 8.5 | 317 | 7.5 | 410 | 2.4 | — | — | 13 | 449 | 22 | 99 |
Our workshop:
FAQ:
1. How can I get the reasonable price efficiently?
-Quantity, specification and 3D drawing will be helpful.
2. What file format are available for you to open?
-DWG, DXF, STP, IGS are available.
3. What is your payment term?
-T/T and Paypal are common, other methods could be discussed.
Company Details
Business Type:
Manufacturer
Year Established:
2006
Total Annual:
300-400
Employee Number:
70~80
Ecer Certification：
Verified Supplier
Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye... Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye...