Tasuns Composite Technology Co., Ltd
| Payment Terms | T/T, L/C |
| Supply Ability | 100cbm/week |
| Delivery Time | 7-10 days for sample |
| Packaging Details | Plywood |
| Deflection | 19mm |
| Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa |
| Closed cell rate | 98% |
| Tensile modulus | 200Mpa |
| Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa |
| Shear strength | 2Mpa |
| Shear modulus | 63Mpa |
| Origin | China |
| Brand Name | Tasuns |
| Model Number | PMI Foam |
| Certification | CE, SGS, ISO |
| Place of Origin | Dongguan, China |
View Detail Information
Explore similar products
Polymethacrylimide PMI Foam Core Fine Holes 51HF 52 kg/m3
Polymethacrylimide PMI Foam Core Density 110 For Sea Fishing
CNC Machined PMI Core For Medical Equipment For Building Sandwich Composite
Fire Retardant Natural White PMI Foam Polymethacrylimide 110
Product Specification
| Payment Terms | T/T, L/C | Supply Ability | 100cbm/week |
| Delivery Time | 7-10 days for sample | Packaging Details | Plywood |
| Deflection | 19mm | Bending strength | 5.5Mpa |
| Flexural modulus | 195Mpa | Closed cell rate | 98% |
| Tensile modulus | 200Mpa | Tensile strength | 3.9Mpa |
| Elongation at break | 2.7Mpa | Shear strength | 2Mpa |
| Shear modulus | 63Mpa | Origin | China |
| Brand Name | Tasuns | Model Number | PMI Foam |
| Certification | CE, SGS, ISO | Place of Origin | Dongguan, China |
| High Light | 19mm carbon composite plate ，195Mpa carbon fiber composite plate ，PMI core carbon composite plate | ||
CNC Machined PMI Core For Medical Equipment
Why PMI foam is good for x-ray medial board?
The application of PMI foam can greatly improve the pressure-bearing capacity of the components: the carbon fiber sandwich structure component made of PMI foam as the core material can withstand a load of up to 1200kg, while the ordinary supporter can only withstand a load of 400kg.
Tasuns PMI foam specification:
1) fine pores
2) coarse pores
3) ultra-fine pores.
| Density (kg/m³) | Model | Mechanical properties at room temperature | ||||||||||
| Compressive strength | Compression modulus | Tensile Strength | Tensile modulus | Elongation at break | Shear strength | Shear modulus | Bending strength | Flexural modulus | Deflection | Closed cell rate | ||
| Mpa | Mpa | Mpa | Mpa | % | Mpa | Mpa | Mpa | Mpa | mm | % | ||
| Testing standard | GB/T 8813-2008 | GB/T 9641-1988 | GB/T 1455-2008 | GB/T 8812.2-2007 | GB/T 10799-2008 | |||||||
| 32 | XK32 | 0.32 | 14 | 0.66 | 28 | 3.8 | 0.28 | 7.6 | 0.86 | 31 | 22 | 99 |
| CX30 | 0.42 | 20 | 0.56 | 39 | 0.69 | — | — | 1 | 31 | 30 | — | |
| 40 | CK40 | 0.6 | 34 | 0.9 | 54 | 1.7 | 0.4 | 19 | 1.3 | 55 | 15 | — |
| CX40 | 0.72 | 29 | 1.2 | 51 | 3.4 | — | — | 1.7 | 58 | 33 | — | |
| 52 | CK52 | 0.9 | 41 | 1.2 | 73 | 1.9 | 0.73 | 27 | 1.6 | 70 | 19 | 99 |
| ZK52 | 0.9 | 51 | 1.3 | 81 | 1.2 | 1 | 26 | 1.5 | 65 | 15 | 97 | |
| XK52 | 1 | 43 | 1.5 | 77 | 3.1 | 0.9 | 24 | 2.1 | 76 | 22 | 99 | |
| 75 | CK72 | 1.4 | 59 | 1.8 | 101 | 2.3 | 1.2 | 40 | 2 | 92 | 13 | 99 |
| XK75 | 1.8 | 72 | 2.4 | 113 | 3.6 | 1.6 | 45 | 3.4 | 117 | 20 | 98 | |
| CX75 | 1.7 | 75 | 2.2 | 89 | 3.8 | 1.2 | 37 | 3.3 | 105 | 23 | — | |
| 110 | XK110 | 3.2 | 138 | 3.9 | 200 | 2.7 | 2 | 63 | 5.5 | 195 | 19 | 98 |
| CX110 | 2.2 | 93 | 3.3 | 160 | 3.6 | 2.2 | 63 | 4.5 | 143 | 21 | — | |
| 200 | XK200 | 8.5 | 317 | 7.5 | 410 | 2.4 | — | — | 13 | 449 | 22 | 99 |
Our workshop:
FAQ:
1. How can I get the reasonable price efficiently?
-Quantity, specification and 3D drawing will be helpful.
2. What file format are available for you to open?
-DWG, DXF, STP, IGS are available.
3. What is your payment term?
-T/T and Paypal are common, other methods could be discussed.
Company Details
Business Type:
Manufacturer
Year Established:
2006
Total Annual:
300-400
Employee Number:
70~80
Ecer Certification：
Verified Supplier
Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye... Tasuns was established in 2006, started with producing carbon fiber and glass fiber products. Following the development of the material industry, and in order to meet the needs of users, Tasuns began to research and develope PMI (Polymethacrylimide) foam core materials in 2011. After ye...